Preparing conductive mica used as conductive material, involves mixing white mica with graphene oxide to obtain raw material mixture, adding a reducing agent to raw material mixture, and performing a reduction reaction.

REN F, ZHANG J, ZHANG A, WU K, LIANG M

Preparing a special unsaturated resin for automobile putty ash, involves mixing and dispersing graphene oxide, surfactant and water ultrasonically, and then ball-milling, filtering, washing and drying it to obtain pre-oxidized graphene.

WU D, XU Y, HUANG H

Preparing smooth artificial synthetic leather involves adding dibutyltin dilaurate to acetone, heating and stirring uniformly, then adding graphene to acetone, ultrasonically dispersing and allowing to stand for cooling.

MAO Z

Preparation method of graphene/polyimide composite material, involves placing graphite powder, sodium nitrate and concentrated sulfuric acid into beaker, stirring, adding potassium permanganate to beaker, stirring, and heating.

CHEN Z

Preparation of composite graphene/polyaniline anti-corrosion coating agent by taking expandable graphite, heating, taking out; taking 3-aminophenylboronic acid and expanded graphite, dispersing, ultrasonicating, heating, and reacting.

DAI L, WANG S, XU Y, ZHU J, MAO J, CHEN T, LI M

Phosphorus-enriched graphene flame retardant, prepared by e.g. uniformly mixing the reaction type phosphorus-containing compound 2-carboxyethyl(phenyl)phosphinic acid and silane coupling agent and smelting.

BAO J, CHEN W, LIU Y

Graphene conductive polymer composite material comprises monomer, oxalic acid, carbon black, triethylamine, stearic acid, graphene oxide, and ammonium persulfate.

ZHANG S