Preparation of vanadium-nitrogen alloy for steel, involves stirring and mixing raw material comprising vanadium oxide or vanadium salt, carbonaceous reducing agent, binder, nitrogen increasing agent, iron powder and stearic acid.

UNANNOUNCED I, ZHANG C

Vanadium alloy reduction smelting reducing agent for smelting ferrovanadium alloy, which is used in infrastructure construction of oil transportation/gas pipeline, building, bridge and rail, is graphene load silicon-zinc-aluminum alloy.

UNANNOUNCED I, ZHANG C

Increasing nitrogen content of vanadium iron nitride used for e.g. high-strength thread steel, involves mixing vanadium source, carbonaceous reducing agent, iron powder, and tin dioxide, ball milling, vacuumizing, introducing mixed gas of nitrogen and ammonia and heating.

ZHANG C

Production of vanadium-aluminum alloy comprises acid leaching vanadium slag, removing iron, adding potassium hydroxide solution into acidolysis liquid, ball milling vanadium containing filter residue, mixing with dilute sulfuric acid solution and carrying out thermal reduction.

ZHANG C

Preparing high quality and low cost vanadium nitride iron alloy comprises e.g. adding vanadium source compound, iron source compound and reducing agent into de-ionized water, stirring to obtain mixed solution, and adding citric acid.

ZHANG C