Preparing graphene heat-dissipating coating material comprises taking graphene, insulating heat conducting filler, graphene dispersing agent, flatting agent, adhesive, antifoaming agent and deionized water.

HU X

Graphene heat-dissipation coating is slurry comprising graphene powder, graphene dispersant, leveling agent, binder, defoamer, insulating heat conducting filler, and aqueous solvent, and has preset viscosity.

HU X

Graphene coating material comprises substrate and graphene coating comprising graphene and aldehyde compound.

FAN B, YANG Y, CHUAN Q, WU Z

Inorganic coating structure for container, comprises inorganic low zinc graphene primer layer, inorganic heat-insulating middle coating, inorganic fire-proof coating and inorganic coating layer from inside to outside in turn coated on substrate.

WANG L, LI Z

Aqueous anticorrosive coating contains component containing aqueous epoxy emulsion, silica sol, aqueous graphene slurry, thixotropic agent and metal anti-rust pigment, and component containing aqueous epoxy curing agent and deionized water.

PANG D

Preparing nano-functional coating used on a glass surface, involves mixing alcohol, silicate compound and organosilane modifier and mixing obtained mixture with dispersion of graphene and water under acidic conditions.

FAN X, ZHANG L, XU X

Aqueous graphene anticorrosive coating comprises water-based resin, graphene dispersion, filler, solvent, defoamer, polytetrafluoroethylene, sodium hexaphosphate, leveling agent, curing agent, dimethyl dicarbonate and deionized water.

ZHANG C, CHE C

Preparing graphene modified nano-titanium ceramic coating useful in interior and exterior wall and floor of public building comprises e.g. using nano-silicon dioxide and nano titanium oxide, performing silane hydrophobization and dispersing.

ZHANG H, DING C, ZHU Y, ZHANG Z, WEN Y

Graphene aging resistant additive useful for building inorganic coating, prepared by e.g. using large-diameter graphene as base skeleton material, uniformly covering with bismuth oxychloride nanoparticles and laying.

CHEN Q, ZAN H

Graphene-based high temperature coating comprises 40-80% high temperature coating body and 20-60% graphene dispersion (comprised of graphene, boron nitride nano-sheets and water).

DAI L, TANG Z, WANG Y, LIU C