Temperature sensing fiber comprises polymer material, temperature sensitive material and polymer material.

TAO G, ZENG S, WANG R

Preparing silver/graphene composite fiber involves preparing large sheets of graphene oxide by the improved Hummers method, preparing graphene oxide water dispersion as spinning solution, and filling the solution into a needle cylinder.

QU J, SHEN M, QIAN J, LI Y, WANG R, HU X

Continuous graphene dry-wet combined spinning method involves dispersing large sheets of graphene oxide in water, adding tetrahydrofuran, adding amine organic solvent, spinning, drying, immersing in coagulation bath, drying and processing.

QU J, WANG R, QIAN J, WU M, HU X, MAO Q, JIA W, ZHANG X

Electrostatic spinning deposition comprises forming a strip of graphene in a spinning pattern, applying an electrostatic field to a substrate, and printing the polymer solution by a probe head for spinning.

HE X, WANG H, CHEN X, WANG R, ZENG J, ZHAN D, XU W, HE C, JIANG W

Graphene polyester fiber comprises skin layer composed of polyester slice which is formed by graphene core layer, skin layer and core layer skin-core composite structure and graphene polyester slice is mixed with polyester chips.

WANG R, ZHI J, HUANG M, LAI S

Preparation of graphene quantum dots/polyvinyl alcohol hollow nanofiber, involves uniformly dispersing graphene quantum dots in polyvinyl alcohol solution to obtain graphene quantum dots/polyvinyl alcohol shell spinning solution.

LI X, HUANG Y, WANG R, CHEN X, ZHAO X, LONG J

Preparing an acrylic fiber involves taking ceramic powder composition and modified graphene, where ceramic powder composition is dispersed in deionized water, and polyacrylonitrile solution is mixed to obtain cortical material.

ZHI J, WANG R, HUANG M, LAI S

Graphene polyester fiber comprises a sheath layer and a core layer composite structure, where the core layer is graphene polyester slice, and the sheath layer is a polyester slice.

WANG R, ZHI J, HUANG M, LAI S

Rapid response graphene fiber comprises graphene sheet winding and forming dual Archimedean spiral structure having sheet interval, oxygen to carbon fiber ratio and X-ray powder diffraction peak position of specified ranges.

GAO C, LIU Y, WANG R, ZHAO X