Preparing graphene underwear fabric used for warming, inhibiting bacteria, and far-infrared heating, by e.g. using graphene nanomaterials, chemical fibers, and artificial fibers, knitting with triangular or row needles, using tension-free dryer, cooling and remaking into graphene underwear fabrics.

YANG Z

Preparing graphene thermal fabric, comprises obtaining graphene oxide powder, cooling polyvinyl alcohol-graphene oxide solution to room temperature, spinning solution on viscose fiber by electrospinning device dying and shaping fabric.

ZENG G, WU M, FU X

Graphene yarn used as fabric raw material, comprises graphene yarn main body composed of graphene yarn reinforcing wire, yarn winding, graphene attached base layer, and graphene layer.

WANG Y

Preparing yak wool loop yarn involves decolorizing the yak velvet through decolorization process, dying the decolorized yak wool through a dyeing process to obtain dyed yak wool, and passing the dyed yak wool through a semi-worsted process.

LI R, HE C, XU Y, QIU D

Constant temperature warm-keeping knitted fabric comprises e.g. dralon orlon, graphene viscose short fiber, viscose fiber, coffee charcoal polyester and bamboo charcoal polyester.

ZHANG Y, GUAN Y

Preparation of graphene composite fiber blended knitted fabric involves weaving knitted fabric with graphene composite fiber blended yarn, terylene, cotton woven and graphene composite fiber that is formed by spinning graphene and terylene.

ZHOU J, LUO W, CAI Y, ZHANG Z

Preparing cotton-type polyester Spandex composite yarn textile useful for woolen sweater, woolen trousers comprise e.g. preparing modified nylon yarn using carboxy-containing graphene oxide, mixing with nylon 6 chips, and melt spinning.

WU X, LAN Z, LIU H, JIANG H

Graphene canvas comprises warp and weft to continuously arranged in triangle structure and/or diamond structure of fabric, where warp yarn is rotating cup for spinning cotton yarn wire by short fiber double twist stranding and twisting.

LIU J, QIN Z, GUO L, JIANG G, MA Z, LAO H, CAO Z, WANG H

Graphene oxide high-inhibition flame-retardant antistatic carpet, which is prepared by cutting velvet, printing-steaming-water washing-dehydrating-stentering, drying-napping-brushing kernel-napping, shearing-wrapping, and packaging.

HUANG X, ZHANG W

Preparing anti-ultraviolet fabric involves extruding graphene, adding into coagulation liquid, cooling, stirring, allowing to stand to solidify into graphene hydrogel film and mixing uniformly by receiving direct current electric field.

LIU H