Producing composite composition of zinc oxide and graphene oxide, comprises e.g. mixing zinc chloride and graphene oxide obtained by mixing e.g. sodium nitrate and sulfuric acid, and treating with water and sodium hydroxide solution.

JO H H, CHOI H K, JEON M H

Synthesis method for preparing flaky zinc oxide/reduced graphene oxide composite material involves taking graphene oxide, and ultrasonically dispersing in absolute ethanol to obtain graphene oxide colloidal solution.

MA Z, SONG P, WANG Q, YANG Z, LIU L

Preparation of self-assembled graphene inline growth nano-rod array composite film, involves immersing metal zinc sheet in graphene oxide solution, reacting, removing, and drying to obtain zinc sheet self-assembled reduced graphene film.

FANG Y, ZHONG Y, YANG S, ZHANG S

Preparing graphene-based thin-film laminate used in e.g. transistor, comprises conducting cycle having e.g. contacting surface of graphene onto substrate with non-metal precursor gas and activating surface of graphene with plasma N times.

PARK C, CHO S, SEO S, SHIN S, KIM T, KIM S, PIAO Z, SEO S A, SHEN Z, PARK C H, CHO S M, SHIN S M, KIM T K, KIM S Y

Producing reduced graphene oxide involves mixing of lumen output particle with aqueous solution of graphene oxide and exposing light, which corresponds to absorption wavelength, where lumen output particle is metal nanoparticles.

PARK H Y, PARK J H, YOO G W

Preparing graphene/zinc oxide nano-line array/three-dimensional foam composite material comprises e.g. chemical vapor deposition, hydrothermal synthesis and chemical vapor deposition.

YUE H, LIN X, GAO X, WANG B, YAO L, GUO E, SONG S, ZHANG H, GUAN E

Preparing metal elemental or metal oxide nano-materials, comprises adding metal nitrate to graphene oxide aqueous suspension under ultrasonic conditions, filtering using quantitative filter paper and completely combusting black graphene.

LI Z, QIU H

Preparation of graphene oxide quantum dot used for producing composite nanomaterial, involves immersing inert electrode of block material in electrolyte solution, cutting and dissociating obtained graphene sheet layers, and dispersing.

XU H, ZHOU Q