Preparing graphene metal-based aerogel comprises e.g. dissolving polymer and transition metal salt in water, cold thawing prepared transition metal oxide nanoparticles, calcining obtained aerogel in protective atmosphere.

ZHUANG Y, SHI B, WANG X

Preparing core shell structure dual metal covalently bonded three-dimensional graphene macroscopic body comprises useful in adsorption and/or catalysis (claimed) and in the field of environmental pollution treatment.

ZHUANG Y, SHI B, WANG X

Preparing nitrogen-doped iron-based graphene gel used for controlling environmental pollution, by mixing graphene oxide, iron salt and urea in solvent and reacting obtained mixed solution.

ZHUANG Y, SHI B

Preparing graphene-based metal-free Fenton catalyst used in environmental pollution treatment, by carrying out acid pickling treatment on waste, soaking treated waste in solution containing additive, drying and calcining product.

ZHUANG Y, SHI B, WANG X

Preparing high molecular gel Fenton catalyst used in field of environmental governance, by dispersing graphene and polymer in water, dissolving iron salt and metal salt in water and mixing.

ZHUANG Y, SHI B

Preparation of alcohol-bridged reinforced porous hydroxy ferric oxide-graphene nanocomposite hydrogel used for preparing product e.g. for adsorbing pollutant by mixing graphene oxide, iron salt and solvent and heating to form into gel.

ZHUANG Y, SHI B, KONG Y, LIU Q

Preparation of graphene involves adding quartz boat and other quartz boat to graphite oxide vessel, uniformly mixing, placing mixture in tubular furnace and then heating, increasing temperature and naturally cooling to room temperature.

CHEN J, CHEN X, MA J, ZHUANG Y

Preparation of alginate-graphene double network nanocomposite gel beads involves stirring graphene oxide, polyvinyl alcohol and sodium alginate, adding divalent ion salt, crosslinking, heating, soaking iron(III) chloride, and UV irradiating.

CHEN J, CHEN X, MA J, ZHUANG Y

Preparing graphene hydrogel involves calcining titanium dioxide nanotubes in presence of inert gas, processing calcined material with acidic, alkaline or neutral aqueous solution, and then adding graphene oxide to processed material.

CHEN J, MA J, ZHUANG Y

Preparation of graphene-protein composite airgel involves adding graphite oxide, protein, and reducing agent in aqueous solution, sonicating to obtain homogeneous solution, heating in water bath to obtain composite hydrogel, and drying.

CHEN J, LI C, MA J, YANG M, ZHUANG Y