Preparation of polyaniline sulfonated graphene composite electrode material used for supercapacitor involves mixing sulfonated polyaniline-graphene composite material and acetylene black, grinding, coating on current collector, and drying.

FENG W, ZHANG Q, FENG Y

Preparing graphene-disulfide polyaniline composite electrode material comprises e.g. preparing the substrate powder and dispersing graphene in de-ionized water, where the ratio of molybdenum trioxide and potassium thiocyanate.

ZHANG Q, YU L, WANG Q, YANG H, LUO Z

Preparing polyaniline-sulfonated graphene composite electrode material for supercapacitor by uniformly dispersing sulfonated graphene in deionized water, and adding aniline monomer to obtained homogeneous solution and dispersing.

FENG W, ZHANG Q, FENG Y

Preparation of sulfonated polyaniline-graphene composite used as electrode material for supercapacitor, involves dispersing sulfonated graphene in water, adding aniline and ammonium persulfate to dispersed solution, polymerizing and drying.

FENG W, ZHANG Q, FENG Y

Preparation of cotton cloth substrate graphene/polyaniline composite material used as electrode material of intelligent clothing, by adding graphite oxide into deionized water, ultrasonically dispersing, and centrifugally separating.

HOU C, LI Y, LIU Q, WANG H, ZHANG Q, XIE H

Manufacture of polyaniline-sulfonated graphene composite electrode material involves mixing polyaniline-sulfonated graphene composite with acetylene black and polyvinylidene fluoride solution, coating on current collector and drying.

FENG W, FENG Y, ZHANG Q