Repairing powder useful for repairing tunnel boring machine of main driving sealing runway, comprises tungsten carbide, cobalt and graphene material, and has preset grain diameter.

WANG C, CAO P, YOU P, FU A, LIAN M, GUO Z

Manufacturing copper alloy for hydrocooling exchangers based on single crystal silicon smelting comprises e.g. preparing furnace material comprising chromium, zirconium, silicon, magnesium, rare earth, and graphene supported cerium powder.

ZHANG Q, ZHANG H, YU G, LI L, MA M, WU B, WANG C, JING L

Preparation of graphene aluminum composite material includes filling nickel salt into pores of foam aluminum, reducing nickel salt to elemental nickel, mixing with carbon-containing gas, heating and pressurizing.

BIAN M, LU K, LI C, WANG C

Preparing graphene aluminum composite material comprises e.g. preparing aluminum film on graphene powder using magnetron sputtering method, adding modified graphene powder into molten aluminum liquid, and heating and curing mixed system.

CHEN C, LU K, LI C, WANG C

Preparing graphene aluminum composite material comprises e.g. providing graphene aerogel, stirring graphene aerogel with aluminum film, compounding graphene powder with aluminum film formed on surface and aluminum matrix.

CHEN C, YANG X, LI C, WANG C, ZHONG X

Preparation of aluminum alloy inner cylindrical wall surface to generate wear-resistant coating involves mixing graphene powder and aluminum powder, adding iron oxide powder and copper-titanium alloy powder, heating, curing and reacting.

TIAN H, YU Y, WANG C, GUO M, TANG Z, GAO J, CUI Y, ZHOU Z, WANG T, ZHANG A

Preparing graphene sheet in situ grown graphene reinforced aluminum matrix complex material comprises e.g. performing surface treatment of graphite sheets to remove surface impurities, and reducing the surface of the graphite sheet.

OUYANG Q, WANG C

Preparing an oxidation resistant bonded copper wire material comprises e.g. purifying raw material of the copper wire, heating, adding the melted copper solution, spraying the graphene liquid, drying and applying the antiseptic oil.

CHENG X, ZHANG L, WANG C

Graphene-reinforced nickel-based composite coating material for aerospace, machinery, automobile, and war industry, comprises self-fluxing nickel-based alloy matrix material comprising graphene as reinforcement.

MA C, HUANG H, WANG C, DONG X