Protective layer structure of pearl copper coating coated with hydroxyl graphene electrophoretic paint, comprises steel base body from inside to outside orderly preparing watt nickel plating layer.

CHEN J, GUO C, LAI H

Processing high-strength, corrosion-resistant plastic electroplating comprises pre-treating plastic piece to be plating by oil-removing coarsening liquid, sensitizing, degumming, activating plastic piece, and electroplating nickel.

LUO W, CHEN J

Composite coating comprises nickel, graphene and chromium, where nickel is used as metal matrix binder, and graphene and chromium are used as reinforcing particles, electrodeposition solution is watts solution includes nickel sulfate.

HUANG S, ZHOU J, CHEN J, SUN K, WEI Y, ZHONG W, HE X, CAI W

Corrosion-resistant coating for injection mold, comprises corrosion-resistant layer formed by electrodeposition on mold base, and wear-resistant function layer formed on corrosion-resistant bonding layer as nickel oxide and graphene coating.

CHEN J

Preparing large size and high quality graphene based on self-limiting nucleation growth comprises e.g. polishing the copper foil, depositing and covering with nickel metal, adding the covered nickel metal copper foil into growth chamber.

ZHANG A, YANG M, CHEN J, ZHAO Y, WEI W, ZHANG X

Preparing graphene film material having improved thermal conductivity and corrosion resistance involves degreasing aluminum substrate, and immersing it in zinc solution, and washing with water, and processing zinc plated material for nickel.

CHEN J, CHEN Y, FAN H, HU L, HUANG Y, LI Q, WANG H, WANG L, WU Q, YANG G, CHEN Z

Film comprises nickel salt, boric acid, reducing agent, graphene, dispersant and surface active agent, where nickel salt is selected from hexahydrate nickel sulfate or hexahydrate nickel chlorite.

CHEN J, FAN H, HUANG Y, LI Q, SUN M, WANG H, FAN X, SHI Q, CHEN Z, GU C, JIE X