Plasma-assisted ball milling preparation of graphene or graphene-like involves placing graphene or graphene-like raw material and grinding balls into plasma auxiliary vibrating milling device, and plasma-assisted ball milling.

WANG S, TAO L, WANG Y

Controlling morphology of molybdenum disulfide/reduced graphene oxide nanocomposite material in lubricating oil additive, involves adding reducing agent to graphene oxide dispersion liquid, adding ammonium molybdate and mixing.

LI C, ZHANG S, LI J, CHEN L

Preparing molybdenum disulfide nano/graphene heterostructure used in fields of semiconductor electronic devices, sensors and catalysis, involves analyzing pure level of molybdate, taking thiourea and ethanol dispersion of graphene.

YANG X, CHAI J, ZHANG D, GU Y, CAO M

Preparing molybdenum disulfide/graphene layered assembly, comprises e.g. under argon gas atmosphere, heating sulfur powder and heating molybdenum trioxide in tubular furnace, then depositing molybdenum disulfide on substrate, and cooling.

FENG Y, ZHENG N, FENG W

Electrode for use in lithium-ion battery, comprises group IV-VI compound and transition metal group VI compound on three-dimensional graphene network.

HUANG Z, YANG H, WANG Y

Preparation of reduced graphene oxide and molybdenum disulfide composite nano paper for supercapacitor electrode, involves adding sodium molybdate hexahydrate and thioacetamide into water, mixing, hydrothermally reacting, and cooling.

HAN W, PAN X, XU S, YU G, ZHOU L

Preparation of ethyl orthosilicate doped three-dimensional graphene/molybdenum disulfide gas aerogel comprises ethanol and ethyl orthosilicate, stirring, adding graphene oxide and molybdenum disulfide, adding acid and hydrothermal reacting.

WU B

Preparation of aerogel e.g. graphene aerogel of two-dimensional material, involves reducing temperature of suspension of two-dimensional material to below melting temperature of solvent having specified melting point and vapor pressure.

DERBY B, KINLOCH I, BISSETT M, CASANO CARNICER G, LIN Y, CASANO C G

Preparation of graphene-supported spherical inorganic fullerene molybdenum disulfide composite material by forming composite material, and performing liquid-phase pulse laser irradiation by e.g. reducing graphene oxide.

LUO T, CAO B, WANG P, YANG S