General synthesis for in situ construction of indium oxide-modified zinc oxide-zinc sulfide heterostructure, comprises e.g. evenly dropwise adding indium nitrate solution to reduced graphene oxide-wrapped zinc powder dispersion under continuous stirring; washing and drying.

ZHANG R, LIANG S, WANG X

Super-lattice material useful in modifying lithium sulfur battery diaphragm, energy storage, electrocatalysis and other fields, formed by self-assembly of titanium-cobalt-oxide nanosheets and polydopamine-reduced graphene oxide aqueous phase.

HUO K, FU J, LUO R, ZHENG Y, ZHANG R

Preparing lithium-ion battery additive for lithium-ion battery involves adding urea solution into suspension, centrifuging, drying, adding aqueous polyvinylpyrrolidone K40, dissolving, cooling, heating, mixing composite under inert atmosphere with stabilized lithium metal powder and sintering.

TONG S, YU X, XU D, GUO P, ZHANG R, ZHOU C, LIU H

Preparing carboxylated graphite alkene involves dispersing the graphene oxide in the solvent to obtain graphene oxide dispersion, adding the graphene oxide dispersion liquid into the reaction kettle, adding citric acid, esterifying agent.

CHEN R, MA H, SHAO X, ZHANG R, JIANG Y, SONG C

Synthesis of rhodium-induced growth of zinc oxide-zinc sulfide heterostructure photocatalyt for producing hydrogen, involves adding zinc powder to graphene oxide dispersion, dripping rhodium chloride trihydrate and mixing obtained rhodium-zinc oxide/reduced-graphene oxide catalyst with thioacetamide.

ZHANG R, LIANG S, WANG X

Nickel particle modified carbon matrix useful in mass spectrometry analysis of metabolic small molecules, prepared by catalyzing nitrogen-doped carbon nano tube/graphene composite sheet structure in situ by apical effect.

ZHANG R, ZHAO H, LIU Y

Preparing graphene-aluminum composite material radiating film comprises preparing mixed solution, oxidizing and neutralizing, diluting and centrifuging, washing, electrophoretic deposition, annealing heat treatment, hot pressing and forming.

TANG S, XIANG B, ZHANG R, ZHANG Q, WU Y

Graphene iron (II,III) oxide solid phase microextraction probe comprises iron (II,III) oxide nanowire arrays and graphene nanocrystals sequentially deposited on the surface of metal wire.

ZHANG R

Nano-nickel ferrite-supported graphene-based absorbing material comprises phosphorus-doped graphene oxide, nanoporous nickel ferrite (NiFe2O4), and paraffin wax.

ZHANG R

Catalyst used for methanation of carbon dioxide, hydrogenation of acetylene for producing ethylene and decomposition of ammonia to hydrogen, comprises graphene aerogel and nickel.

ZHANG R, HU F, FENG G, WANG D