Hole sealing solution of self-repairing high corrosion-resistant sealing material, for preparing micro-arc oxidation coating used in metal surface treatment fields, comprises predefined amounts of silazane, siloxane, silane coupling agent, graphene, polyisocyanate, pH regulator and deionized water.

GAN H, ZHANG Y, LIU X, ZHU H, CUI X

Preparing zinc-coated graphene oxide composite anti-corrosion coating, comprises e.g. preparing zinc-coated graphene oxide powder, and then mixing zinc-coated graphene oxide powder, epoxy resin and organic solvent, placing it in a ball mill, then ball milling, adding curing agent and mixing.

QIAN J, TANG F, XIE H

Automobile top cover aluminum alloy shell, comprises aluminum alloy substrate whose surface orderly provided with a transition layer, an intermediate layer and a corrosion resistant coating, where the middle layer formed by stacking two layers of modified silicon dioxide.

ZHANG L

Method for processing high-strength corrosion-resistant stainless steel pipe fittings, involves taking pretreatment pipe fittings, performing ultrasonic rolling on outer surface, washing pretreatment pipe fittings with deionized water after rolling and vacuum drying pretreatment pipe fittings.

XU J, HU X, SANG C, RUAN J, ZHOU Q

Cationic dopamine-functionalized graphene aqueous anticorrosive coating used for preparing anticorrosive coating in corrosion application, comprises cationic dopamine-functionalized graphene material and aqueous resin emulsion, where graphene material is uniformly dispersed in aqueous resin emulsion.

WANG L, ZHU X, LIU S, LU G, ZHAO H, XUE Q

Electroplating zinc-cadmium alloy and coating hydroxy-graphene modified electrophoretic paint comprises preparing zinc-cadmium alloy coating, phosphating layer and hydroxy-graphene modified electrophoretic paint coating.

GUO C, LAI H, CHEN M, XIA L

High adhesion fingerprint-resistant hot-dip galvanized steel sheet comprises e.g. middle substrate, first galvanized layer, first passivation solution, first fingerprint resistant layer, second galvanized layer and second passivation layer.

GONG K

Corrosion inhibition on substrate, involves applying sealing solution comprising nanomaterial dopant to anodized surface of substrate, and drying sealing solution on substrate to form sealing layer comprising corrosion inhibiting compound.

STEELE L, PUJAR V V, SMITH B A, POTEET S A