Preparing magnetic reduced graphene oxide composite material used to remove quinolone antibiotic from water, comprises mixing oxidized graphene with ethylene glycol, and adding sodium citrate, iron(III) chloride hexahydrate and urea.

WANG Y, TANG Y, XIAO L

Graphene-based nano-metal composite material comprises metal particles having specific value of particle size supported on graphene having three-dimensional porous foam structure matrix having pore size of specific value.

CHENG G, JIANG Z, LI N, WANG W

Purification of ionic liquid involves preparing multiradical modified graphene oxide, then preparing magnetic nano material-loaded graphene oxide and absorbing impurities in ionic liquid by magnetic nano material-loaded graphene oxide.

LI Q, ZHAO X, JI G, FENG Y, TU J, LI T

Water pollution treatment nano adsorbing material comprises nano tourmaline, modified activated carbon, nanoclay, modified graphene oxide and synthetic resin compound.

ZHAO B

Preparing molecular imprinted estrogenic endocrine disruptor involves hydrothermal synthesis of magnetic graphene by dissolving ferric chloride hydrate in ethylene glycol to obtain mixture, which is agitated in ultrasonic agitator.

HUANG Y, LI P, LI Y, WU J, KOU X, LI J

Preparing modified graphene-based iron oxide nano-composite material, useful in the absorption of heavy metal ions in sewage, preferably cadmium ions, comprises e.g. dissolving 3-mercaptopropyl triethoxysilane in a solvent, and hydrolyzing.

LIU J, LV X, YUAN S, DU H, HE W

Graphene oxide material for magnetic composite material for water treatment, comprises graphene compound, and edge of graphene oxide is linked with carboxyl group and hydroxyl group.

SONG C, WANG L, FU N, FU X, HAO S, MIN L

Multilevel pore structure of graphene fiber used as electrode material in super capacitor, where in the multilevel pore structure, the graphene fiber has specific outer diameter, specific length-diameter ratio, and specific surface area.

WEI F, CUI C, QIAN W

Making titanium dioxide/chitosan/graphene oxide composite material involves dispersing graphene oxide into dilute acetic acid, adding chitosan powder and titanium dioxide, dripping glue liquid into sodium hydroxide solution, washing, drying.

CHENG Y, HE H, LUO S, YANG C, ZENG G, TU Y

Forming hollow tubular composite material by ultrasonic dispersion treating dispersant, hollow tubular graphene multi-porous polymer material and N,N-dimethyl acetamide and vacuum drying formed graphene liquid with graphite absorption layer.

HU X, XIAO C, ZHAO J