Preparing manganese ferrite magnetic photocatalyst based on multi-component composite system, comprises e.g. adding graphene oxide and potassium tetrachloropalladate into water, and carrying ultrasound treatment to obtain first solution.

DENG Y, ZHANG R, DONG H, LOU H, WAN J, RUAN S

Preparing anti-icing coating comprises e.g. transferring colloidal solution to surface of substrate, heating substrate with colloidal solution attached to volatilize a dilution solvent, continuously heating, and completing expansion of expandable microspheres in colloidal solution.

ZHANG R, LI J

Preparing nitrogen-doped reduced graphene oxide- based aerogel with a highly regularized structure used in adsorption material, comprises mixing graphene, nitrogen containing compound and reducing agent, performing gelation reaction to obtain hydrogel precursor; drying, carbonizing and cooling.

ZHANG R, MENG Q

Multilayer film of graphene oxide-polymer microgel used as adsorbent for removal of dye, is formed by alternately depositing polymer microgel and graphene oxide on quartz sheet or silicon wafer substrate by layer-by-layer self-assembly.

JIANG W, LI L, WANG J, MIAO S, ZHANG R, SHI X, LI X, WANG L, MA S

Preparing polyurethane thermally conductive anticorrosion coating comprises determining deployment amount of hydroxy-type aqueous-based polyurethane, controlling quantitative addition of graphene oxide dispersion, adding film-forming aid and dispersant and carrying out constant temperature stirring.

CUI X, ZHANG R, MA P

Modified polyisoprene rubber useful for making polyisoprene having tensile strength and fatigue resistance, prepared by physically and uniformly blending polyisoprene containing polar component and second polar substance, and then vulcanizing.

YANG Y, ZHANG R, XU Y

Method for preparing pore-rich thin layer graphene, involves pre-treatment of oil raw material using catalytic oil slurry or residual oil through delayed coking treatment to obtain coking liquid product as pre-processing raw material oil.

ZHANG R, XU Q, BI Q, WANG X, LIU Y, WANG L, WU M, HE S, ZHAO Q, ZHANG H

Preparing nano-magnetic graphene oxide-polyaniline composite material used to adsorption and purification of heavy metal ions and organic dyes, involves taking magnetic graphene oxide, adding aniline and hydrochloric acid, stirring ultrasonically, and controlling mixing temperature.

DONG L, GUO G, ZHANG R, QU S, WANG Y

Graphene water reducing agent useful as cement and concrete dispersant, comprises e.g. isopentenol polyoxyethylene ether, pentaerythritol tetraacrylate, 2-acrylamide-1-methylpropanesulfonic acid, unsaturated phosphoric acid esters, graphene oxide, 3-mercaptopropionic acid and initiator.

ZHANG H, PANG Y, GUO J, ZHANG R

Preparing flavor diglyceride oil comprises e.g. placing crude oil, enzyme preparation and chelating agent in shaking table, performing vacuum reaction, using gas adsorbent to collect reaction gas, distilling reaction product molecule performing molecular distillation, extracting mixture.

SUN D, XIN X, DU Z, LV L, WANG S, LI Q, ZHANG R, XU H, WANG X