Preparing graphene-composite anticorrosive coating by ultrasonically dispersing reduced graphene oxide in organic solvent, dissolving epoxy resin in organic solvent and mixing reduced graphene oxide dispersion and epoxy resin solution.

QIAN X, SHI S, ZHAO C

Organic microsphere supported three-dimensional graphene cadmium sulfide composite catalyst used for photocatalytic hydrogen generation comprises styrene organic microsphere, graphene oxide, and cadmium acetate and dimethyl sulfoxide.

CAO X, XU J, WANG L

Converting carbon dioxide into graphene useful in energy storage and electronics, comprises contacting metal with gaseous carbon dioxide, and irradiating surface of metal with laser beam to convert carbon dioxide into graphene.

ZHAO C, DONG J, HUANG Y, QIAN X

Method for preparing foam nickel composite material, involves preparing methyl alcohol solution with oxidation graphene and surfactant, obtaining oxidation graphene suspension solution, and obtaining uniform suspension in kettle.

QIAN G, SUI Z, ZHOU J, ZHOU X, ZHANG Z, YANG S

Preparation of graphene-silica transparent film involves dispersing graphene in deionized water or ethanol, adding silica sol into graphene dispersion to obtain graphene-silica sol, and dipping treated glass sheet into graphene-silica sol.

FAN Y, QIAN X, WEN J, ZHANG Y, ZHAO C, YAN K, DENG S, YANG J

Preparation of modified graphene oxide-polyimide in-situ-grafted composite material involves dispersing aminated graphene oxide in N,N'-dimethylacetamide and 4,4'-diaminodiphenyl ether, adding pyromellitic dianhydride, and heating.

FANG X, FENG H, LIU X, LI X, QIAN J, ZHUANG Q, HUA J

Metal sulphide/graphene/vulcanization nickel composite thin film material preparing method, involves filling metal nickel substrate with mixed solution, and forming stainless steel component with vulcanization nickel composite material.

QIAN X, WANG K, ZHANG X, ZHAO C, ZHANG Z, ZHANG Y

Method for preparing nickel phosphide/graphene composite thin film material, involves immersing metal substrate in dispersion liquid, performing hydro-thermal reaction in kettle, washing thin film material, and drying and storing material.

QIAN X, SUN C, WANG Q, ZHAO C, ZHANG J, CHEN H, ZHANG Y

Graphene/clatharate composite material for thermoelectric material, comprises graphene/cobalt-germanium-selenium component.

FANG B, LIANG Y, LI F

Preparation of graphene involves contacting metal and composition containing graphene oxide under conditions sufficient to reduce portion of graphene oxide to graphene.

ZHAO C, MIN S, DONG X, QIAN X