Large-scale low-temperature thermal reduction preparation of graphene by preparing graphite oxide solution by traditional Hummer's method, adding flocculating agent, naturally settling, washing, drying, low-temperature crushing and heating.

BAI Y, GAO W

Cellulose nanofiber/graphene reinforced starch film comprises starch, polyvinyl alcohol, plasticizer, cellulose nanofiber and graphene oxide.

QIN Z, WEI X, ZHANG M, GAO W, MO L, LIAO M, ZHU Q

High-strength high-rigidity graphene-modified polypropylene material comprises specified amount of homopolypropylene, graphene, E-glass fiber, enzymatic lignin, compatibilizer, antioxidant, lubricant, and coupling agent.

WANG N, BAO H, GAO W, LIU C, SUN J, XU H

Coating composition useful for solar cell back board, comprises graphene filler, resin, titanium dioxide, solvent, curing agent, and auxiliary agent.

BAI Y, SHA Y, SHA X, GAO W

Preparing solar battery back board comprises e.g. using graphene based filler and resin slice, uniformly mixing, orderly carrying out mixing, extruding, shaping and biaxially stretching to obtain the solar battery back board.

BAI Y, SHA Y, SHA X, GAO W

Conductive graphene modified polyamide composite material comprises low viscosity polyamide, graphene, toughening agent, compatibilizer agent, antioxidant.

GAO W, BAO H, WANG N, LIU C, GE X, ZHANG J

Graphene composite acrylonitrile butadiene styrene multi-functional resin comprises preset amount of acrylonitrile butadiene styrene resin, modified graphene, and compatibilizer.

BAI Y, SHA Y, SHA X, GAO W

Method for preparation of functionalized graphene reinforced polyolefin composite material, involves pretreating graphene or graphene oxide, premixing with polyolefin matrix, granulating, cooling with water and molding.

BAI Y, GAO W, SHA X, SHA Y

Oxidized graphene adhesive comprises solvents and graphene oxide is prepared by performing hydrophilic treatment, coating, drying and bonding.

GAO C, LI Z, ZHANG C, CHANG D, CHEN C, GAO W, GUO Y, HAN Y

Self-fusion graphene fiber prepared by e.g. vacuum drying the oxidized graphene fibers, then soaking the dried fibers in the solvent and completely swelling the fiber.

GAO C, CHANG D, LI Z, GAO W