Preparing yellowing-resistant thermoplastic polyurethane comprises heating isocyanate and dihydroxy water repellent, adding polyglycol, 1,4 butanediol, graphene, anti-yellowing agent, antioxidant, catalyst, and monohydroxy water repellent, and baking.

HE P

Preparing polyurethane thermally conductive anti-corrosion coating involves adding isophorone diisocyanate and polypropylene glycol to stirring device through feed port according to preset ratio.

CUI X, ZHANG R, MA P

Graphene/aqueous polyurethane composite material used in coating, comprises polyether glycol including polytetrahydrofuran ether glycol and tetrahydrofuran-propylene oxide copolymer glycol, polycarbonate diol, chain extender, triethylamine, organic phosphorus flame retardant, and reducing agent.

JIANG Y, ZHANG Z

Epoxy corrosion-resistant waterproof coating comprises epoxy resin, modified polyurethane, zinc oxide, nano-silicon dioxide, ethyl acetate, nano-molybdenum disulfide, graphene oxide, sodium lignosulfonate, barium titanate, active diluent, curing agent, cross-linking agent, and plasticizer.

ZHANG W, ZHANG P, CAO W, YIN D, ZHU X, LI Z, WANG H

Coating comprises e.g. polyurethane emulsion prepared by using aminoporphyrin grafted titanium dioxide as chain extender, antifoaming agent, film-forming auxiliary agent, flatting agent, dispersant, wetting agent, and water.

LIU X, LIU C, CHEN Y, WANG W

Preparation of composite material for e.g. aerospace applications, involves preparing modified graphene oxide, preparing polyurethane product, dissolving modified graphene oxide in dimethyl formamide, adding to polyurethane product solution, ultrasonically processing, and transferring to mold.

YUAN H, JI C

Modified epoxy polyurethane sealant comprises e.g. bisphenol A epoxy resin, vinyl ester resin, silicon dioxide, aluminum oxide, graphene oxide, octadecylamine, silane coupling agent, propylene oxide, diethyltoluenediamine, and solvent.

ZOU W, LIAO C

Flame-retardant polyurethane aqueous emulsion comprises polyhexylene adipate, toluene diisocyanate, 2,2-dimethylolpropionic acid, flame-retardant filler, graphene oxide, bactericide, antifoaming agent, and water.

HUANG H, HU Y, ZHU Q

Preparing impact-resistant graphene polyurea composite coating on surface of impeller, comprises e.g. mixing isophorone diamine, 1,4-bis-sec-butylaminobenzene, tetrahydroxypropyl diamine and amino-terminated polyether and solidifying.

JIA J, JIA X, WANG Z, LI Y, YANG J, SUN Y, SUN J

Preparing anticorrosive material, involves dehydrating polyether polyol and castor oil under vacuum, drying dimethylol propionic acid, dehydrating acetone, mixing, adding isophorone diisocyanate, heating and adding e.g. crosslinking agent.

XU X, CAO D, GUAN C