国家/地区 中国（8）
IPC部 C（8）
IPC大类 C08（8） C09（8）
IPC小类 C08G（8）
IPC C08G018/66（8）
发明人 WANG B（3） HUI L（2） JIN C（2）
LI C（2） LI H（2） SHI Z（2）
WANG J（2）
公开年 2020（8）
申请年 2019（8）
专利权人 ANHUI XINDAL.（2）

Preparing graphene oxide modified aqueous closed isocyanate curing agent involves stirring and mixing the weighed graphene oxide, diisocyanate and methyl ethyl ketone to obtain a mixed solution A, and then heating in the reactor.

WU S, LI C, PAN C

Preparing graphene modified flame retardant waterborne polyurethane coating and adhesive comprises e.g. adding ammonium molybdate, nano silver and 1,5-naphthalene disulfonic acid to terephthalic acid and deionized water and stirring.

DUAN B, WANG Q, WANG H, DIAO S, WANG X, LI X, TANG Z

Material used for manufacturing high-hardness coating for protecting aluminum alloy, comprises fluoropolyurethane polymer materials, organic solvents, graphene fluoride, and PTFE dispersion in preset mass ratio, and polyimide fibers.

JIANG G, TANG K, LI C, ZHAO Y, PENG M, ZHAN B

Preparation of pipeline heavy anticorrosion polyurea protective material involves reacting polyester polyol or polyether polyol and isocyanate, and adding component comprising graphene-modified amino-terminated polyether and chain extender.

WANG B, YUE C, ZHANG H, LIU X, HUANG Z

Preparing anticorrosive and antistatic machine tool coating involves adding graphene oxide to absolute ethanol, and then adding aluminum chloride solution and alkylphenol polyoxyethylene ether under sonication.

WANG B, SHI Z, LI H, JIN C, HUI L, WANG J

Preparing aqueous-based polyurethane coating by dispersing graphene oxide in deionized water, adding cobalt chloride and calcium titanate, reacting, washing, drying, adding acetone, polyol and catalyst, stirring, cooling and emulsifying.

WANG B, SHI Z, LI H, JIN C, HUI L, WANG J

High-hardness, anti-sagging polyurethane water-based functional coating comprises e.g. amorphous poly alpha olefin (APAO) modified polyurethane aqueous resin, film-forming auxiliary agent, nano glass microbeads, thickener and white graphene.

ZHANG W, KANG L, YAO D

Polyurethane resin comprises graphene, macromolecular diol, dimethylolpropionic acid, N-methylpyrrolidone, diisocyanate, deionized water, acetone, catalyst and crosslinking agent.

BAI W