Nanonickel-loaded graphene composite wave-absorbing material is layered composite material comprising nickel nanoparticles having particle size of preset value, grown on graphene sheet, and polyaniline coated on graphene sheet.

FENG D

Graphene-nano nickel composite wave-absorbing material is layered nano composite wave-absorbing material containing graphene sheet layer, nano nickel particles loaded on graphene sheet layer, and polyaniline coated on surface particles.

FENG D

Nanonickel-loaded graphene composite wave-absorbing material is layered composite material comprising nickel nanoparticles having particle size of preset value, grown on graphene sheet, and polyaniline coated on graphene sheet.

FENG D

Composite wave-absorbing material is layered composite material comprising iron oxide nanoparticles having particle size of preset value, grown on graphene sheet, and polyaniline coated on surface of nanoparticles-loaded graphene sheet.

FENG D

Manufacture of graphene-nano-nickel wave absorbing material involves mixing surface-treated graphite oxide, polyethylene oxide-polypropylene oxide-polyethylene oxide terpolymer, aniline monomer and ammonium persulfate, and reacting.

FENG D

Preparation of nanonickel-loaded graphene composite wave-absorbing material involves dripping ammonium persulfate solution into mixture containing e.g. surface-treated graphite oxide, stirring, filtering, washing and drying.

FENG D

Preparation of graphene supported nano nickel absorbing composite material by adding graphite to hydrochloric acid solution, stirring, washing with deionized water, drying, and adding with potassium persulfate and phosphorus pentoxide.

FENG D

Graphene-loaded nano-nickel wave absorbing material, prepared by preparing a mixture of pre-oxidized graphite, surface processing the pre-oxidized graphite, dispersing, heating the dispersion solution, centrifuging and vacuum drying.

FENG D

Nanocomposite wave absorbing material is layered nanocomposite wave absorbing material having hollow iron oxide nanoparticles grown on graphene sheet layer.

FENG D

Preparation of absorbing material nanocomposite for production of graphene/hollow ferroferric oxide/polyaniline nanocomposites involves adding graphite powder into hydrochloric acid solution, stirring, and repeatedly washing.

FENG D