Preparing graphene-coated electronic compound comprises mixing calcium source and aluminum source compound, placing mixture into an organic solvent, stirring, placing transparent solution into high-pressure reaction vessel, and heating at a high temperature.

QING T, KHAN K, LI N, YIN J, QING D

Oxide ceramic and two-dimensional material composite hydrogen-resistant coating comprises co-deposited layer of zirconium and yttria-stabilized zirconia, intermediate layer of aluminum oxide doped two-dimensional material, and aluminum oxide ceramic layer, which are sequentially coated on substrate.

YE J, LI T, WANG L, LUO M, JIANG L, LI Z, LIU H, LI S, LIU W, LV Z, MI J, HAO L, YU Q, WANG W

Graphene sensor composite heat protection structure, comprises substrate layer, graphene sensitive layer, nitride isolation layer, alumina protective layer, and high temperature ceramic protective coating, where substrate layer is provided with a graphene sensitive layer.

LI M, ZHANG H, WANG J

Preparing graphene-reinforced copper-based complex material comprises sintering raw materials by hot pressing or spark plasma (SPS) to convert amorphous carbon film into graphene microcrystals.

YANG Y, ZHANG F, XIA L, LI F

Forming graphene layer for e.g., LEDs, by mixing carbon source with horizontally oriented molten solvent, precipitating carbon source to form graphite layer across molten solvent, and separating graphite layer into a set of graphene layers.

SUNG C, HU S C, LIN I, YU C

Preparing stannic oxide composite coating comprises mixing tin dioxide and graphene for isostatic compaction and sintering to obtain grapheme/tin oxide composite ceramic target and controlling magnetic sputtering.

DU Y, WANG G, CUI L

Forming graphene layer used in e.g. transistors, solar panels, involves mixing carbon source with molten solvent, precipitating carbon source from solvent to form graphite layer, and separating graphite layer into several graphene layers.

SUNG C, HU S C, LIN I, YU C, SONG J