Conductive ink comprises conductive nano-metal and a graphene dispersion liquid including a graphene, where graphene dispersion liquid is a first slurry, and the conductive ink further comprises a slurry sub-material.

ZHANG X, HU M, ZHANG M, XIE X, ZHU K, ZHU Y

Preparation of rare-earth conductive graphene up-conversion nanotube involves carrying out solvothermal reaction of gadolinium(III) hydroxide-trivalent ytterbium ion-trivalent erbium ion nanotube and processing using graphene.

YANG M, DAI L, MA J, BAO B, QI L, YAO Q, CHENG R, CHEN L

Preparing composite conductive film comprises e.g. mixing graphene and potassium permanganate solution, heating, stirring reaction, filtering, washing and then mixing chitosan solution, polyvinyl alcohol solution and reducing agent.

LONG S, YIN L, CHEN Y

Amino oxidized graphene/cellulose acetate composite material containing polypyrrole.

LU X, YUAN Y

Manufacture of graphene/nano-silver conductive film involves forming base film, mixing graphene oxide dispersion and hydrazine hydrate, adding silver nitrate aqueous solution, reducing, adding dispersion to base film, and hot-press drying.

LIN Q, LI L

Preparing graphene/silver nanowire transparent conductive film used in e.g. solar cells, by dissolving graphene oxide prepared by Hummers method in water, and carrying out ultrasonic dispersion to obtain graphene oxide aqueous solution.

LIN R

Manufacture of gold graphene by adding graphene into penetrant, dispersing, adding gold ion compound solution, contacting graphene lattice with gold ions, carrying out ion penetration reaction, drying and packaging.

KE L, LIANG S, SITU R

Preparation of steam-reduced graphene oxide conductive polymer composite film used in conductive sensing, involves.

ZHU Z, LUO H, ZHOU X, WANG H, YI G, WANG Z, TANG Z

Transparent conductive film used for LEDs or film solar energy battery comprises sequentially stacking conductive nanotube line layer set on substrate, graphene film and function adjusting layer.

XU M

Electrical conductor for use in electronic devices, has first conductive layer that includes graphene which is p-doped with p-type dopant, formed in first surface facing second conductive layer and second surface.

SOHN H, SHIN W, WOO Y S, SUN X, XIN Y, YEO R, SOHN H S