Preparing gold nano-particle by quickly reducing graphene-based self-assembled multilayers comprises e.g. taking polyethyleneimine and polyacrylic acid as polyelectrolyte, and processing self-assembly technology by taking hydrazine hydrate.

AN Q, ZHANG Y, LI X

Synthesis of composite material involves mixing mixed solution of graphene oxide and silver-ammonium hydroxide solution, adding isopropanol, stirring, placing resultant mixed solution in sealed container, and irradiating electron beam.

CHENG L, JIAO Z, JIANG Y, PAN Y, WANG Y

Water suspension useful as antitumor agent against human or animal tumors, comprises graphene oxide nanoflakes and nanoparticles of metallic platinum deposited on surface of graphene oxide nanoflakes.

GRODZIK M, HOTOWY A, JAGIELLO J, JAWORSKI S, KUTWIN M, LIPINSKA L, SAWOSZ CHWALIBOG E, WIERZBICKI M, SAWOSZ C E

Graphene-nano nickel composite thermoelectric thin film is prepared by adding solution containing graphite oxide into container, immersing pre-treated copper plate as negative electrode and iron sheet as positive electrode and reacting.

LIU Y

Method for manufacturing carbon-metal composite, involves reacting composition with specific amount of graphene, providing carbon compound in composition, and providing carbon nanotube with carbon-metal composite.

GONG S Y, LEE S Y, CHOE H, LEE C, LI X, LI Z, CUI X, KONG X, GONG S

Preparation of graphene/ferriporphyrin/gold nanoparticle composite material involves mixing graphene oxide aqueous solution and ferriporphyrin suspension, adding chloroauric acid, ultrasonically mixing, and adjusting pH.

WANG W, KONG F, YU Z

Manufacture of graphene-nano-nickel wave absorbing material involves mixing surface-treated graphite oxide, polyethylene oxide-polypropylene oxide-polyethylene oxide terpolymer, aniline monomer and ammonium persulfate, and reacting.

FENG D

Manufacture of graphene-nano-nickel wave absorbing material involves mixing surface-treated graphite oxide, polyethylene oxide-polypropylene oxide-polyethylene oxide terpolymer, aniline monomer and ammonium persulfate, and reacting.

FENG D

Preparation of graphene supported nano nickel absorbing composite material by adding graphite to hydrochloric acid solution, stirring, washing with deionized water, drying, and adding with potassium persulfate and phosphorus pentoxide.

FENG D

Preparation of graphene composite material involves exfoliating graphite oxide, mixing obtained graphene oxide solution and to-be-mixed composite material including pyrrole, drying, and exposing resultant product to laser or sunlight.

CHENG H, QU L