Preparation of water-soluble fluorinated graphene quantum dots for e.g. biosensor, involves adding fluorinated graphene to alkaline composition, adding modified fluorinated graphite to mixed acid and dialyzing filtrate.

WANG J, YANG S, GONG P

Graphene structure used as white fluorescent luminescent material, consists of graphene sheet, and graphene quantum dots having armchair-type end surface at edge portion of sheet coated with polyhedral oligomeric silsesquioxane.

HAINO T, SEKIYA A

Large-scale preparation graphene quantum dots, comprises adding graphene oxide into first solvent to obtain first dispersion solution, adding reducing agent, reacting, carrying out solid-liquid separation and cooling to obtain crude product.

ZHANG M, ZHANG L

Production of graphene involves applying physical force to liquid dispersion of dispersing agent containing polyaromatic hydrocarbon oxide, and carbon-based material comprising graphite, and forming graphite into nano graphene flakes.

SOHN K N, YOO K H, KWON W J, LEE K S, YANG S B, KIM I Y, LEE M J, LEE J Y, SOHN K, YOO K, KWON W, LEE K, YANG S, KIM I, LEE M, LEE J, LI M, LI J

Production of aqueous dispersion of few-layer graphene nanosheets used for coated article, involves mixing graphite particles with perfluorosulfonate ionomer in aqueous liquid, and arranging ionomer as thin and continuous layer.

JULIUS D, ZIN M, DIVIGALPITIYA R, KORBA G A, KIM M

Graphene composition for graphene molding comprises organic compound, graphene with flakes, and dispersing agent.

HASEGAWA SHOJI, KAMIYA NAGISA, HASEGAWA S, KAMIYA N

Synthesizing reduced graphene oxide on a substrate from seedlac, comprises preparing the seedlac solution in alcohol having specified carbons, dipping the substrate into the solution, and heating the substrate which is a metallic sheet.

SHYAM K C, MANISH K B, TAPAN K R, SUMITESH D, RANJAN K S, YASHABANTA N S, ASHIT K P, VIKAS C S, CHOUDHARY S K, BHADU M K, ROUT T K, DAS S, SAHU R K, SINGHBABU Y N, PRAMANICK A K, SRIVASTAVA V C

Graphite-type carbon raw material used as graphene precursor, has rhombohedral system graphite layer and hexagonal system graphite layer in ratio more than preset value, as measured using peak intensities specific planes of layers.

HASEGAWA S, KAMIYA N, SHOJI H, NAGISA K, HASEGAWA SHOJI, KAMIYA NAGISA, SHEN Y

Forming polyaniline/reduced graphene oxide composite involves dispersing graphene oxide in aqueous solution of anionic emulsifying agent to form dispersion, dissolving aniline oligomer in solvent and mixing oligomer solution with dispersion.

BOCCHINI S, CHIOLERIO A, PORRO S

Graphene modified thermoplastic phenolic resin preparation for friction material comprises mixing phenol compound, aldehyde compound, and acid catalyst to obtain phenolic resin, and mixing phenolic resin and graphite.

TANG Y, JIANG C, LIU W, SONG Q