Diffusion film for small display, comprises UV resin layer coated on surface of base material, and prepared using acrylic resin oligomer, acrylic resin monomer, photoinitiator, scratch-resistant agent and adhesive.

LIU Q, MA H

Economical and practical aqueous-based epoxy graphene bottom-surface-in-one coating comprises aqueous based epoxy resin, curing agent, modified graphene oxide and nano-alumina and prepared by modifying graphene into graphene oxide, modifying by nano-alumina and mixing with aqueous based epoxy resin.

WANG B, XU Y, LIU Q, NAN D

Preparing modified fluorocarbon coating comprises e.g. preparing titanate, absolute ethanol and glacial acetic acid, adding co-doped titanium oxide nanoparticle, ultrasonically dispersing, reacting, and mixing co-doped titanium oxide/graphene aerogel microsphere and silane coupling agent.

ZHU R, CHEN X, LIU Q, WANG W, YIN Z, WANG Q, LIN J

Paint useful for children's whiteboard, comprises aqueous resin, modified nano-zinc oxide synergistic bentonite composite modifier, hydrophobic modified nano-stabilizer, wetting and dispersing agent, film-forming aids, interface modification coupling agent and water.

WEI Y, TIAN G, YANG X, HAN Y, LIU Q

Modified fluorocarbon coating useful for corrosion resistant air purifying paint in building manufacturing and decorating process comprises fluorocarbon resin, epoxy modified polyacrylate resin, co-doped titanium dioxide/graphene aerogel microspheres, titanium dioxide, leveling agent and benzoin.

ZHU R, CHEN X, LIU Q, WANG W, LIN J, WANG Q, YIN Z

Economical and practical acrylic acid graphene bottom surface-integrated coating useful for prolonging service life of bad working condition e.g. seawater corrosion comprises acrylic resin, curing agent, modified graphene oxide and nano alumina.

WANG B, LIU Q, XU Y, NAN D

Economical and practical polyurethane graphene bottom surface coating useful for prolonging service life of bad working condition, comprises polyurethanes, curing agent, modified graphene oxide and nano aluminum oxide.

WANG B, LIU Q, XU Y, NAN D

Preparing poly-indole modified graphene oxide/acrylic fluorine boron composite antifouling coating used for cleaning biological fouling on surface of hull, involves e.g. mixing, removing impurities in mixed solution and unreacted pyridine triphenylborane, collecting solid powder, and freeze-drying.

WANG J, ZHU J, SUN G, LIU Q, CHEN R, FAN H, YU J

Preparing chitosan-modified graphene oxide composite coating, comprises adding chitosan to acetic acid solution, adding graphene oxide, preparing product A and product B, centrifuging, preparing product D, washing and with epoxy modified polyurethane resin.

ZHANG H, WANG J, LIU P, LIU Q, SUN Y, CHEN R

Fluorinated graphene supported metal organic frameworks/modified epoxy resin superhydrophobic coating material comprises modified epoxy resin, fluorinated graphene supported metal organic frameworks nanomaterials and curing agent, where the curing agent is diethylenetriamine and triethylenetetramine.

WANG F, CHEN T, CAO Y, JING M, WANG H, ZHANG Z, WANG Q, ZHANG F, LI W, CHANG H, LIANG Y, LIU Q, ZHANG S