Cement base fluorine-containing copolymer emulsion useful for preparation of superhydrophobic concrete comprises fluorine-containing monomer e.g. perfluorononylethylene, alkyl acrylates and/or alkyl methacrylates, nonionic and/or anionic surfactants, silica, titania and/or graphene oxide, and water.

ZHANG B, JIANG Z

Preparing graphene oxide modified styrene-acrylic emulsion useful in anticorrosion of cement-based material, comprises mixing graphene oxide buffer solution and styrene-acrylic monomer mixed solution, mixing obtained emulsion and silane coupling agent and ultrasonically dispersing.

WANG P, WANG X, LI S, YIN B, WU C, HOU D

Conductive polymer composite material comprises cement, medium sand, conductive filler, polymer, silica fume, expansion agent, dispersant, defoamer water reducing agent, and water.

WANG L, TIAN Y, GAO P, LI X, SHAN H, XU S, SUN X, WANG R, ZHANG J

Polymer cement waterproof coating comprises liquid material and powder material, liquid material comprises modified styrene-acrylic emulsion, antibacterial agent, thickener and film forming agent and the powder comprises portland cement.

HONG L

Micro-nanocrystalline core composite material in cement-based material for concrete, comprises graphene oxide and/or chemically grafted modified graphene oxide, hydrated calcium silicate, and high molecular polymer.

ZHANG L, WANG D, LI H

Graphene-reinforced ceramic matrix composite material obtained by mixing graphene, photo-curing resiN and photoinitiator, adding ceramic powder, mixing dispersant, 3 dimentional photo-curing molding, slicing, degreasing and sintering.

LIU S, CAI W, LI Q

Waterproof type cement based coating comprises graphene, ethyl orthosilicate, silane coupling agent, absolute ethyl alcohol, aqueous ammonia and deionized water as superhydrophobic material, inorganic powder and water reducing agent.

WANG F, ZHAO G, ZHOU J, WANG H, WANG Z

Preparing superhydrophobic JS waterproof coating comprises e.g. mixing water-soluble cationic surfactant and water, adding graphene, silicate gel solution, silanization reagent, emulsion, then adding quartz sand, carbon nanotubes, stirring.

ZHAO G, ZHOU J, WANG F, WANG H, WANG Z

Frost inhibiting enhancing agent useful for cement bricks comprises e.g. acrylic monomer, acrylate monomer, cationic monomer, emulsifier, sodium hydroxide solution, graphene oxide sheet layer suspension and initiator aqueous solution.

LV S, ZHU L, GU C, HU H

Method for preparing graphene oxide modified polymer cement waterproof paint, involves preparing graphite oxide solution and acrylic ester polymer emulsion, and obtaining graphene oxide modified polymer cement waterproof paint.

JU H, LV S, ZHOU Q