Light-guiding fiber for photocatalyzing carbon dioxide to prepare methanol is skin-core structure, including light guiding layer, photocatalytic layer covering light guiding layer and protective layer covering photocatalytic layer, where light guide layer contain high polymer with light guide effect.

ZHOU N, ZHANG K, ZHANG Y, DONG Y, LIU Y

Preparing polyethylene terephthalate (PET)-based graphene conductive fiber for preparing textile raw material, by melt-blending graphene/PET conductive masterbatch and PET natural chips, feeding to extruder, drawing and heat setting.

JIANG Z, JIA Z, ZHANG Z, GUO Z, QI Y, HOU Z, WANG H, PU C, WANG Q, DING Z

Preparation of radiation-proof polyester fibers used in e.g. home textiles, involves forming homogeneous dispersion of graphene/ethylene glycol solution, polymerizing, forming highly dispersed graphene/polyester and melt-spinning.

ZHANG G, XU Y, CHEN Y, TANG L, WU G

Preparation of highly dispersed graphene-nylon 6 composite fiber, involves carrying out micro mechanical peeling of graphite into graphene in aqueous solution of caprolactam to obtain graphene-caprolactam aqueous solution.

ZHANG G, XU Y, CHEN Y, TANG L, WU G

Preparation of graphene/nylon 6 fabric with permanent far infrared healthcare function used e.g. for clothes and blanket comprises weaving graphene/nylon 6 composite fiber on fabric, adding additive, and performing high-speed melt spinning.

GAO C, HAN Y, CHEN C

Preparing graphene-nylon nanocomposite fiber comprises mixing nylon chips and graphene or modified graphene, extruding, granulating to obtain graphene-nylon masterbatch and melt-spinning the graphene-nylon masterbatch.

SHA X, SHA Y, BAI Y

Preparation of graphene-poly(p-phenylene benzobisoxazole) composite fiber involves vacuum heating and vacuum defoaming graphene/poly(p-phenylene benzobisoxazole) polymer, and carrying out coagulating bath treatment.

HUANG Y, LI J, HU Z, LIU L, SUN D, SONG Y, LI Y

Preparation of graphene/polyimide composite fiber involves adding graphene or graphene oxide to polyamic acid solution to obtain graphene/polyamic acid spinning stock solution, polycondensing, and wet spinning or dry spraying wet spinning.

CHEN D, DONG J, WANG Y, ZHANG Q, XIA Q, YIN C