Preparing polyamidoamine functionalized graphene-hyperbranched aqueous polyurethane useful in e.g. synthetic leather, fabric coating, comprises e.g. functionalizing and reducing graphite oxide using polyamide-amine with terminal amino group.

WANG X, FENG J, LUO X, WEI M, WANG Y, ZHAO W

Manufacture of sulfonated graphene oxide/high-solid-content aqueous polyurethane emulsion involves reacting dimethylolpropionic acid, sulfonated graphene oxide dispersion and oligomer diol-isophorone diisocyanate prepolymer, and emulsifying.

FENG J, WANG X, LUO X, WANG Y, BAI P

Coating material for improving surface conductivity of industrial graphene microchip, comprises industrial graphene microchip and nanosilver particles, where nanosilver particles grow on surface of industrial graphene microchip.

WANG Y

Preparing magnetic nanocrystalline cellulose grafted oxidized graphene surface molecular imprinted polymer for fluoroquinolones medicine, involves polymerizing magnetic nanocrystalline cellulose grafted oxidized graphene composite.

OUYANG X, SUN X, WANG Y, WANG N, YANG L

Halloysite graphene oxide composite catalytic preparation of poly epsilon-caprolactone comprises acidifying calcined halloysite, silylation, stirring with graphene oxide solution and ring-opening polymerization with epsilon-caprolactone.

MA R, HU P, XU L, FAN J, WANG Y, NIU M

Tetrapolyurethane film used for medical, electrical and mechanical needs comprises diisocyanate, polyol, graphene, 2-acrylamido-2-methyl-1-propanesulfonic acid, styrene-acrylonitrile copolymer, heavy chain extender and catalyst.

HE J, WANG Y, YANG B

Polypyrrole-functionalized graphene nanocomposite light confinement material is composed of polypyrrole-modified graphene oxide.

ZHANG C, WANG Y, WANG A, QIAN J, LONG L

Preparing graphene-aqueous polyurethane composite material involves adding sulfuric acid in dry beaker and mixing graphite, sodium nitrate and potassium permanganate under magnetic stirring for two hours to obtain mixture.

WANG Y

Preparing graphene-hollow nano ferroferric oxidepolyaniline composite material comprises adding graphite powder and sodium persulfate, stirring, diluting, washing, filtering, heating, reacting, controlling, dropping and vacuum drying.

WANG Y

Method for improving dispersibility and interface compatibility of graphene in epoxy resin, involves ultrasonically dispersing graphene oxide and disproportionate rosin purified product dehydroabietic acid, and dissolving in co-solvent.

HUANG J, NIE X, HU F, WANG Y, LI X