Preparation of graphene thermally conductive film involves coating slurry prepared by dissolving graphene oxide powder in solvent, and defoaming resultant, on substrate, drying, winding, trimming, heating, cooling, and vacuum rolling.

ZHOU B, ZHOU R, LI F, LU J

Preparing graphene heat-conduction heat-dissipation composite material by mixing shear thickening system containing thermally-conductive filler with graphite raw material and subjecting mixed liquid to mechanical shearing.

YANG Y, WANG X, QIU S, HE C, LEI C, ZHANG J, LEI S

Preparation of thermal conductive film involves taking graphene slurry, adding dispersant, stirring, adding binder, mixing, adding a thickener to adjust the viscosity, stirring, coating graphene thermal conductive paste and rolling.

CHEN X, MA N

Preparing high thermal conductivity graphene doped composite sheet comprises e.g. mixing natural graphite with acid solution, adding catalyst and expandable intercalation agent, washing, drying, ball milling, vacuum-rotating and sintering.

WANG T

Low-fold thermal conductive graphene film used as high flexible thermal conductive device comprises high-tenacity graphene film and planar graphene sheets.

GAO C, PENG L

Preparing polyethylene terephthalate/graphene composite thermal conductive film involves placing graphene in vacuum mixer by adding anhydrous ethanol, stirring and filtering to get mixed graphene/ethanol slurry and using desktop coater.

LIN Q, LI L

Preparing graphene/carbon nano tube composite material comprises manufacturing stage graphene oxide, providing graphene acid material into to the carbon nanotube fiber, and adding graphene acid bonding phase of the carbon nanotube fiber.

KIM Y, LIANG Z, YANG X

Preparing graphene composite material comprises e.g. grinding graphite oxide, mixing with diethylene glycol and sonicating, placing diethylene glycol containing zinc acetate solution, adding graphite diethylene glycol solution, and stirring.

WANG S

Functionalized graphene used for preparing polyorganosiloxane comprises active molecule and graphene.

XU Y, LI Y, HODGE S, FERRARI A, LIN Y

Preparation of graphene/graphite powder composite material used as heat conductive filler by mixing oxidized graphene aqueous dispersion and graphite powder, dispersing, spray-drying, pre-expanding, and high-temperature calcining.

SU Y, SONG X, SU Q