Processing angle steel in transmission line angle steel tower useful in e.g. circuit devices and systems, comprises e.g. drilling angle steel, cutting, treating steel in cleaning solution, dipping treated steel in metal salt solution, and spraying steel with protective coating.

ZHAO Y

Coating useful for preventing fresh water shell vegetable from adhering comprises flexible epoxy sealing bottom coating, organic silicone anti-adhesion middle coating and fluorine silicone oil modified silicone rubber surface coating from inside to outside.

WENG M, ZHANG S, WANG Y, LU G, LI J, ZHANG H, SONG Y, HUANG J, DING Q, ZHANG Y

Preparing electro-galvanized surface super-hydrophobic film layer useful in galvanized product, comprises e.g. uniformly coating layer of substrate reagent on surface of electroplating zinc product, natural drying, forming base layer on surface of electro-galvanized product, leveling, and coating.

SHI H, WAN H, PAN G, FAN W, CHEN W

Preparing anti-corrosion composite coating used in anti-carrosion field of metal material comprises coating amino silane coupling agent on metal substrate, coating epoxy resin adhesive, pre-curing, coating polysiloxane adhesive on epoxy resin adhesive layer, and coating hydrophobic nano particles.

MA X, YUAN S, DONG Y, ZHOU M, XIE B, ZHAO T, XING J, PENG S, YU Y

Preparing super hydrophobic and oleophobic coating useful for oil-water separation, comprises stirring fluorine-containing organic silane in nano-particles dispersed ethanol solvent to obtain uniformly mixed suspension, coating on upper surface of substrate material along with adhesive and curing.

GONG J, GE Y, MA J

Preparing superhydrophobic composite coating useful in technical field of coating materials, comprises e.g. adding nanoparticles and organic binder into absolute ethanol, magnetically stirring, mixing by anhydrous ethanol-water mixed system, hydrolyzing and condensing, cooling, spraying and drying.

ZHAO X, TENG Y, WU X, WANG S

Anti-scour radiation heat insulation coating for titanium alloy, comprises bonding primer layer and high emissivity layer, where primer layer of bonding layer is formed by solidifying primer layer of the bonding, and high emissivity layer is formed by curing high emissivity coating.

LU M, LIU L, YI M, ZHANG Y, NING L, WU L, WANG F, WANG X