Dual-phase metal aluminide composite material comprises dual-phase mixture of nickel-aluminum and nickel aluminide as main crystal phase, and graphene as reinforcing phase.

CHEN Y, SONG Y, LIU W, WANG Y, ZHOU B, ZHAO D

Synthesis of three-dimensional graphene-reinforced nickel based composite material involves taking glucose or citric acid, nickel nitrate hexahydrate and soluble salt template sodium chloride, mixing, and dissolving in deionized water.

HE C, FU K, ZHANG X, ZHAO N, SHI C, LIU E, HE F, LI Q, LI J

Stirrer head modified graphene reinforced nickel-based alloy powder comprises vanadium, strontium, indium, aluminum, titanium, cobalt, molybdenum, boron, erbium, graphene, and nickel.

CHEN K, DU Y, TANG Y, XU A

Preparing silver-nickel-graphene alloy material comprises e.g. adding silver nitrate and aqueous ammonia into pure water, cleaning, drying, sieving the graphene composition powder, ball milling and sieving.

CHEN T, LI G

Surface modification of lanthanum-magnesium-nickel-based hydrogen storage alloy for preparing electrode, involves pulverizing hydrogen storage alloy, sieving, mixing obtained alloy powder with graphene powder, and ball-milling.

HUANG H, WANG X, XIE W, YU W

Preparation of graphene/nickel-based composite material, involves mixing nickel or nickel alloy powder with oxidized graphene solution, ball-milling to obtain nickel or nickel alloy powder-graphene oxide mixed liquid, and drying.

CHEN L, MAO L, SHEN M, WANG P

Manufacturing graphene-reinforced nickel-based composite material, by mixing nickel sulfate, reducing agent and graphene oxide solution, reducing to form nano-nickel powder, adsorbing using graphene, lyophilizing, reducing and molding.

CHEN L, MAO L, SHEN M, WANG P