Manufacturing method for graphene device, involves providing substrate, where substrate comprises insulating layer and semiconductor layer, forming source/drain contact plug on back gate electrode.

ZHU H, LIU X, ZHONG H, LIANG Q, JIN Z

Graphene filled polymer-based composite material comprises thermoplastic resin, graphene microsheet, coupling agent, and lubricant.

LIU X

New dendritic macro-molecule functional graphene loaded noble metal nano catalyst used for e.g. allyl alcohol hydrogenation.

GUO Y, LI Z, LIU J, LIU X, PENG S

Preparing modified graphene oxide, comprises preparing modified graphite oxide, adding water to resulting modified graphite oxide, performing ultrasonic treatment to obtain a modified graphene oxide solution, and drying the solution.

HOU S, HUANG H, LU H, LIU X, MA H

Modification of methyl phenyl silicone resin comprises adding graphene oxide and long chain aliphatic hydrocarbon in solvent to completely dissolve, and adding powder-shaped solid in methyl phenyl silicone resin solution.

BAI H, BAI Y, LIU L, HUANG Y, JIANG B, MENG L, LIU X

Method for manufacturing rare earth modified graphene, involves stirring water soluble carbon source compound with purified water, dispersant and rare earth compound with aqueous solution, and oxidized graphite powder with mixed solution.

CHEN C, WANG C, ZHONG B, GUO X, YANG X, LIU X, JIA X

Graphene pattern forming method, involves drawing auto-CAD document format of conductive film pattern input optical fiber laser marking machine, and placing graphene coated glass on laser marking machine.

CHEN K, HUANG H, HUANG S, LIU X

Nitrile composite material used for graphite alkene micro chip, comprises nitrile resin with graphene micro sheet.

GUO H, LIU X, WANG Z, YANG J, YANG X, ZHAN Y, ZOU Y

Synthesis of water-dispersible polyaniline/graphene composite material comprises reducing graphene oxide into graphene, dispersing, adding aniline, dripping oxidizing agent and inorganic acid solution, and polymerizing.

LUO J, LIU X, JIANG S, WU H, WU Y

Graphene device structure for use in complementary metal oxide semiconductor device, has semiconductor doped region and graphene layer that are formed as drain region and source region of device structure respectively.

LIANG Q, JIN Z, WANG W, ZHONG H, LIU X, ZHU H, YE T