Electrochemical preparation method of molybdenum disulfide/graphene composite electrode used for dye-sensitized solar cell, involves mixing graphene oxide/lithium perchlorate, and ammonium tetrathiomolybdate/potassium chloride.

LI S, MIN H, NI Y, SUN L, XU F, ZHU C

Electrophoresis depositing black graphene quantum point modified graphene thin film by adding black graphene quantum point with phosphorus-containing organic solvent solution, water bath ultrasonic mixing, adsorbing, and adsorbing.

LI S, XU F

Preparation of black phosphorus graphene nanosheet involves adding black phosphorus crystal and organic solvent to agitation barrel, stirring mixture and rotating, processing mixture and dispersing, centrifuging mixture, and filtering.

LI S, MIN H, SUN L, XU F, ZHU C, LI Z, XIA W

Making three-dimensional black phosphorus quantum dot-graphene nanosheet composite material by stirring ethanol solution of black phosphorus quantum dot and graphene oxide nanosheet ethanol solution and performing solvothermal reaction.

XU F, ZHU C, TONG R

Preparation of black phosphorus alkene-graphene composite material hollow microsphere used for, e.g. sensor by preprocessing oxide dispersion, spraying into liquid helium, rapidly freezing, freeze-drying and subjecting to reduction reaction.

LI S, MIN H, NI Y, XU F, ZHU C, LI Z, TONG R, XIA W

Composite carbonyl-sulfide-nano graphene dye-sensitized solar energy battery electrode, has composite graphene thin oxide film directly deposited on surface of carbonyl-sulfide nano array.

XU F, LI X, MIN H, ZHU C, DONG H, SUN L, TAN S, WANG H, LIU X, SUN B, DI W

Method for applying macroscopic graphene material, involves utilizing macroscopic graphene material including porous graphene foam and graphene thin film as sound absorbing material.

HE L, XU F, YIN K, WANG S, WU X, CHEN Z, BI H, SUN L, ZHOU Y, WAN N, WAN S, WANG H, WANG J, WU H

Preparation of graphene film for counter electrodes of dye-sensitized solar cells, involves spraying graphene oxide dispersion on preheated substrate, and reducing formed film by hydrazine reduction and high-temperature calcination.

HUANG J, XU F, PENG F, CHEN K, DING N, GUO L, SUN L, ZHANG Y, ZHU Y, WANG H

Preparation of graphene thin film used for coating involves adding graphite oxide in solvent, ultrasonic dispersing to form graphene oxide dispersion liquid, placing substrate on heating platform, and heating dispersion liquid on substrate.

WAN S, BI H, HE L, XU F, WU X, XIE X, YIN K, SUN L, XIE R

Preparation of hydrophobic graphene sponge used for environmental protection by dispersing graphite oxide in solvent, freeze-drying, reducing under high temperature, annealing, cooling, modifying by gold nanoparticle and reducing.

HE L, XU F, WU X, ZHOU Y, YIN K, XIE X, BI H, SUN L, WAN S