Preparing graphene loaded nano-silver-nickel alloy composite powder comprises e.g. mixing graphite powder and sulfuric acid, reacting with sodium nitrate and potassium permanganate mixed solution, dialyzing, and ultrasonically processing.

WANG L, ZHAO D, CUI W, FU J

Manufacture of graphene involves forming primary filter cake by reacting specified amount of benzene and anhydrous aluminum chloride, forming secondary filter cake and tertiary filter cake, and drying deionized tertiary filter cake.

DAI T, ZHOU P, ZHAO D

Preparing composite material comprises adding graphene oxide to copper sulfate solution and treating, adding sodium hydroxide and hydrazine hydrate solution and stirring, heating, cooling, filtering and washing, and drying washed product.

YAN F, WANG Y, WANG L, ZHAO D

Temperature-sensitive method for preparing graphene oxide by initiating polymerization to N-isopropylacrylamide, and grafting polymer onto surface of oxidized graphite alkene, where terminal end is provided with azide group.

CHANG J, SUN X, LI Y, DUAN Q, ZHAO D

Polyaniline-graphene oxide-nano nickel composite material used in chemical industry field involves preparing crystalline flake graphite, performing semi-permeable membrane dialysis, reacting and ultrasonically treating.

HAN C, CUI W, FU Y, ZHAO D, YAN F

Preparation of graphene-loaded nano-nickel composite powder material used for e.g. catalyst, involves mixing nickel chloride-ethylene glycol solution, hydrazine hydrate solution and graphene oxide solution of crystalline flake graphite.

HAN C, ZHAO D, FU Y, YAN F, WANG T

Manufacture of lithium ion battery involves growing multi-layer graphene on nickel foam, punching graphene into circular negative thin sheet, and placing in battery casing with positive pole thin sheet and supporting component.

GONG B, LIU J, DONG C, FENG Q, ZHAO D, WANG H, LI Q

Ferrocene-grafted polyethyleneimine-graphene composite material used for electrochemical biosensor is prepared by reacting ferrocene-grafted polyethyleneimine and graphene oxide solution.

CHEN Y, XI F, YAN F, ZHAO D