Metal material for flame retardant steel structures, for preparing fire-proof boards, includes a metal substrate, and a fireproof coating prepared by coating a fireproof coating on the surface of the metal substrate.

LI Z, LI X

Processing hardware surface anticorrosion treatment, comprises e.g. mixing hydrochloric acid solution and pyrrole monomer to obtain solution A, mixing hydrochloric acid solution and ammonium peroxodisulfate to obtain solution B, mixing the solutions, filtering and drying to obtain polypyrrole powder.

GU S, LUAN J, DENG K

Anti-corrosive paint useful for metals in metal anticorrosion, comprises e.g. photocurable coating precursor including pentaerythritol oleate, (3-mercaptopropyl)triethoxysilane and 2-hydroxy-2-methyl-1-phenylpropanone, and nano-silicon dioxide.

CAI Y, LI H

Corrosion resistant preparation for spiral steel pipe, comprises coating liquid, which is prepared using phenolic resin, copper oxide, hexagonal boron nitride, ferroferric oxide, potassium chloride, cobalt oxide, graphene dispersant, curing agent, deionized water, and aluminum tripolyphosphate.

YI Y

Spaying process of titanium ceramic water-painted aluminum plate involves pre-processing, cleaning aluminum plate, preparing material, where spraying material is titanium ceramic water-proof paint and curing agent, and spraying using spray gun, and air drying.

JIANG Y, JIANG H

Synthesizing aggregated graphene-reinforced aqueous polyurethane corrosion resistant coating comprises ultrasonically dispersing graphene oxide in deionized water, adding phosphoric acid, adding aniline and ammonium persulfate, coating on protected metal steel plate surface rod coating, and drying.

WANG T, ZHU Z, WU L, JING L, NING Y, GENG H

Crosslinkable polyethylene composition comprises polyethylene matrix resin, polar molecules, peroxide crosslinking agent and anti-corrosion filler, where polar molecules are epoxy resin, polyester resin, isocyanate, isocyanate oligomer, acrylic ester and/or acrylic ester oligomer.

REN D, SUN X, ZHU H

Anti-corrosion treatment method for a steel structure iron tower resistant to marine climate involves sequentially carrying out oil removal, rust removal, and dehumidification on steel structure surface, and spraying anticorrosive primer on the surface of steel structure to form primer layer.

MA Y, WENG S, YAN T, WANG Z, YANG Z, LIU X, JIANG Q

Aqueous coating composition for cold chain containers, comprises primer including aqueous epoxy emulsion, aqueous polyurethane emulsion, aqueous epoxy curing agent, and topcoat including aqueous epoxy emulsion, aqueous acrylic emulsion, and aqueous polyurethane emulsion.

MA X

Combined use of coating and impressed current cathodic protection technology for metals, by coating primer layer, conductive coating and topcoat layer on metal surface, and connecting to negative and positive electrodes.

DENG P, HU J, WANG G, LIU W, HUANG H