Preparing nanoparticle capable of continuously tuning physical property used for preparing composite material, involves mixing graphene oxide and barium titanate nanoparticles with deionized water, dispersing ultrasonically to obtain dispersion, placing dispersion liquid in atomization cup.

ZHEN L, YU Y, LI Y, SHAO W

Freezing and casting of interlayer toughened fiber composite material involves soaking woven fiber cloth in water-soluble polymer solution containing nanomaterials, directionally freezing on metal mold, freeze-drying to obtain aerogel-loaded fiber cloth, soaking in matrix resin, molding and curing.

HUANG Y, LIU L, WANG B, LU F, LI D, HU Z

Preparing modified graphene reinforced polymer barrier material by heating modified polymer and organic solvent, dispersing graphene by organic solvent, mixing, crystallizing, adding polymer substrate mixture, precipitating and filtering.

WANG R, YANG F, LIU G

Preparing graphene/rubber composite material based on spray drying and hot pressing vulcanization involves adding graphene in deionized water, stirring obtained mixture, adding rubber in water, and then adding vulcanization agent.

LI Y, LIN Z, XU F, HE X

Preparation of high conductive and high electromagnetic shielding flexible composite material involves freezing oxidized graphene, freeze-drying, reducing and compressing.

LI Y, CHEN R, XU F, HE X, PENG Q, LIN Z

Preparing bacterial cellulose/polyaniline/graphene film material used as electrode in supercapacitor, comprises adding acidified graphene into a surfactant, dispersing in hydrochloric acid solution, adding aniline monomer and stirring.

LIU R, MA L, YUAN G, ZHANG F, LI E

Preparation of graphene/poly-p-phenylene benzobisoxazole composite copolymer film, involves reacting aminated-graphene with diaminoresorcinol dihydrochloride and terephthalic acid, molding, immersing in phosphoric acid, and drying.

HUANG Y, LI J, LI N, ZHAO S, HU Z, WANG Y, LI Z, YI G

Polyimide/fluorinated graphene composite film is obtained by dispersing graphene in polyimide base component.

BAI R, LI Y, NIU Y, ZHAO J

Preparation of temperature-sensitive resistor material involves ultrasonically treating graphene-grafted sodium styrene sulfonate, N,N-dimethylformamide and polyvinylidene fluoride mixed solution, and drying.

LI C, LIN F, SONG Y, SUN Q, WANG F

Grafting graphene oxide on surface-modified carbon fiber by oxidizing graphite, peeling oxidized graphite in solvent, functionalizing graphene oxide, functionalizing carbon fiber surface and processing graphene oxide on carbon fiber surface.

HUANG Y, JIANG Z, LI Y, LIU C, LIU L, MOU C, ZHANG C, ZHENG X