Preparing nickel particle composite powder loaded with graphene, comprises e.g. taking hexahydrate nickel sulfate, sodium sulfate, ammonium sulfate and sodium dodecyl sulfate dissolved in ultra-pure water, and magnetically stirring.

ZHANG Y, ZHOU M, SU S, XIANG S, WU J, LI X, YANG X, LIU P

Graphene-nicotinic acid silver plating solution comprises silver salt, complexing agent, buffer, conductive salt, additives, graphene and water, and prepared by dissolving silver salt, complexing agent, buffer and conductive salt in water.

ZHOU M, LI X, CHEN X, LUO C, QUAN J, DENG H

Preparing aluminum alloy product with layered double hydroxide-graphene oxide silane composite coating comprises preparing mixed metal salt suspension by aluminum salt and zinc salt, and performing hydro-thermal treatment.

XU Q, HE Z, ZHOU M, ZENG Y, SHEN X, MIN Y

Plating solution comprises copper sulfate heptahydrate, tris(ethylenediamine), ammonium sulfate dihydrate, sodium sulfate decahydrate, dispersant, nano graphene sheet and tungsten powder.

DING Y, ZHU Z, YE Z, ZHOU M, CHEN X, CHEN B, ZHANG Q, ZHU C, ZHANG S

Preparing self-supporting reduced graphene oxide coating involves taking brass sheet as cathode and copper sheet as anode in composite plating solution, adding phosphoric acid to adjust pH value and applying pulse current.

ZHOU M, MAI Y, JIE X, ZHANG L

Preparing composite coating for used in preparation of self-lubricating coating, involves dispersing graphene oxide powder and disodium ethylenediaminetetra acetate in deionized water to obtain mixture, which is dispersing by ultrasonic.

ZHOU M, MAI Y, JIE X, ZHANG L

Producing copper-based self-lubricating composite coating involves subjecting ultrasonic dispersion of carboxylated carbon nanotube and/or graphene polystyrene in aqueous solution of composite surfactant to form dispersion liquid.

ZHOU M, MAI Y, JIE X, ZHANG L