Preparing three dimensional net-shaped silicon carbide nanowire used in e.g. national defense military industry, involves mixing polymolybdenumcarbosilane vinyltriethoxysilane-graphene oxide powder or poly(N vinylguanidine powder, pore forming agent powder, and cracking.

ZHAN J, TAO Q, MAO S, ZHENG Y, WANG Y, LIANG J, HUANG W, YAO R

Preparing silicon carbide honeycomb ceramics, comprises e.g. stirring walnut shell carbon powder, graphene powder, silicon fluoride, silica sol, pore-forming agent, and sintering aid, adding dispersant and extrusion aid, extruding, heating, cooling, and immersing in resin solution.

GUO F, CHEN L, LU S, YANG F, TANG X, ZHANG L

Energy-saving wear-resistant zirconium corundum composite hollow ball casting material used in e.g. blast furnace, comprises zirconium corundum aggregate containing zircon sand, silicon carbide, organic fibre, silicon micro powder, pure calcium aluminate cement, water reducer and additive.

WO J, GU C

Preparing porous silicon carbide high-temperature heat-insulating tile, involves mixing poly(N-vinylguanidine) (PVG) powder and silicon carbide-reduced graphene oxide ceramic filler powder by ball milling, drying and grinding, finally adding graphite powder pore-forming agent, and mixing uniformly.

PAN C, WU Y, MAO S, GUAN Y, LIANG J, ZHENG Y, HUANG W, YAO R

Preparation method of high-strength low thermal conductivity ceramic gas material gel, involves sintering silicon dioxide fiber gas gel, pouring graphene dispersion liquid into mold, and immersing SiO2 nanofiber gas gel.

TANG Y, ZHAO K, LI C, LI F, QIU H, DANG W

Preparing carbon strips for pantograph carbon slides, comprises e.g. kneading calcined product powder and pitch coke, adding graphene material, blank making, pre-pressing viscous mixture, calcining and performing quality inspection to prepared carbon bar by measuring instrument.

SHI G

Preparing porous silicon nitride ceramic material, involves preparing graphene oxide aerogel from graphene oxide dispersion liquid and amino trimethylene phosphonic acid crosslinking agent using aqueous ammonia as alkali catalyst and adopting hydrothermal method.

TAN C, ZHANG C, LIN W