Preparing graphene oxide reinforced polymethyl methacrylate/carbon microsphere composite material involves carrying out a hydrothermal reaction using glucose solution as carbon source, and after the reaction, washing product various times.

FEI J, HU S, ZHU Y, WANG Y, ZHOU M, LIU Z, GU Y

Preparation of graphene oxide modified composite phase change microcapsule by taking graphite powder, potassium permanganate, concentrated sulfuric acid and deionized water, and reacting with absolute ethanol and silane coupling agent.

ZHOU J, CUI Y, MA J, MU M

Manufacture of crosslinked polyacrylate-based graphene nanocomposite agent used for coating leather, involves adding specified amount of carbonylated polyacrylate and aminated graphene oxide to reactor, adjusting pH, and reacting.

MA J, ZHANG L, GAO D, LU B, ZHANG W, LV B

Graphene oxide/aqueous polyurethane acrylate composite emulsion used in preparation of anticorrosive coating for polished metal surface, contains vinyl monomer, diisocyanate, polyester polyol, hydrophilic chain extender and graphene oxide.

WANG H, LI J, FEI G, GUO D, SUN L

Frost inhibiting enhancing agent useful for cement bricks comprises e.g. acrylic monomer, acrylate monomer, cationic monomer, emulsifier, sodium hydroxide solution, graphene oxide sheet layer suspension and initiator aqueous solution.

LV S, ZHU L, GU C, HU H

Preparing high solid content of graphene oxide grafted polyacrylate composite liquid by adding e.g. graphene oxide and thionyl chloride into bottle, then processing, and adding double bond of graphene oxide into the bottle, then dripping.

GAO D, LI C, MA J, ZHANG W, LIANG S

Preparation of ultrasonic-assisted polyacrylic ester/amino-modified graphene oxide composite leather coating agent involves dispersing graphene oxide, thionyl chloride, and dimethylformamide, refluxing, and adding dimethylformamide.

GAO D, LI C, MA J, ZHANG W, ZHOU Y, ZHA J

Preparing pigment printing adhesive comprises dissolving ammonium persulfate in deionized water and then adding emulsion initiator solutions to obtain polyacrylate emulsion and then graphene water solution and stirring.

LI C, MA J, ZHANG W, GAO D

Preparation of acrylic resin/graphene oxide nanocomposite leather finishing agent involves mixing graphene oxide suspension with methyl acrylate, ethyl acrylate, butyl acrylate, hydroxyethylacrylate, emulsifier and lauryl sodium sulfate.

LI D, LV S