Preparing conductive polyethylene terephthalate fiber comprises e.g. mixing graphene oxide, conductive carbon black and ethylene glycol, adding terephthalic acid and stabilizer, and carrying out high temperature esterification reaction.

LI N, FAN Y, PAN X, PANG D

Modification of polyester masterbatch for spinning application, by adding graphene material dispersion to reaction system during esterification of terephthalic acid and ethylene glycol, and polycondensing obtained esterification product.

SUN H, MA J, WANG S, LV D, TANG D

Preparing differential epigenetic involves mixing an oxalic acid solution, hypochlorous acid solution, bismuth vanadate, graphene oxide, zinc oxide, rutile titanium oxide, and hydrotalcite for hydrothermal reaction, and grinding.

FAN Y, LING R, LI Q, TAO R, ZHANG F, HU C

Preparing differential purified terephthalic acid involves mixing bismuth molybdate, graphene oxide, hypochlorous acid solution, zinc oxide, white carbon black, potassium titanate whisker with hydrofluoric acid aqueous solution.

FAN Y, TAO R, HAN W, HU C, YANG X

Hydrophilic antistatic graphene modified polyester chip, prepared by esterifying, adding catalyst, performing polycondensation reaction and performing underwater pelletizing.

HU S, WANG X, HU C, DONG H

Preparation of graphene-reinforced polyester fiber involves esterifying terephthalic acid and ethylene glycol, adding antimony acetate and coated graphene containing graphene powder and aluminum sulfate solution, heating, and spinning.

QIU L

Terylene comprises modified graphene, prepared by e.g. oxidizing graphene, modifying oxidized graphene with an aminosilane coupling agent, placing modified graphene in an organic solvent and then ultrasonically dispersing.

LI F

Preparation of radiation-proof polyester fibers used in e.g. home textiles, involves forming homogeneous dispersion of graphene/ethylene glycol solution, polymerizing, forming highly dispersed graphene/polyester and melt-spinning.

ZHANG G, XU Y, CHEN Y, TANG L, WU G

Catalyst loaded graphene modified polyester comprises graphene powder or graphene oxide powder loaded with catalyst, ethylene glycol, and terephthalic acid , and obtained by esterification and polycondensation reaction.

HU S, HU C, DONG H, WANG X

Manufacture of flame-retardant anti-dripping polyester fibers for e.g. clothing, involves polymerizing terephthalic acid, ethylene glycol, and agent including phosphorus-based flame retardant and graphene oxide, and melt-spinning.

CHEN Y, HOU Z, WANG S