Modified silicon graphene material used in external wall thermal insulation materials, contains silicon dioxide aerogel, inorganic fiber, sodium silicate, zeolite powder composite microspheres, cement, and water reducing agent.

XIE L, ZHONG J, WU X

Preparing defect-free graphene oxide for preparing graphene heat-dissipating film, involves reacting carbon source under acidic condition, reacting graphene quantum dots and amine substance, mixing mixed system containing aminated graphene quantum dots, graphene oxide, and dispersing agent.

SUN S, ZHANG L, WU X

Silicon-based bonded graphene radiating copper-clad ceramic substrate comprises copper foil layer orderly set from up to down, ceramic layer and silicon-based bonding graphene coating set on lower surface of ceramic layer.

LIANG X, JIA T, WU X, SUN X, YANG H, ZHANG G, RUAN S

Well wall reinforcing composition for crushing stratum, comprises cement, cementing agent, interface strengthening agent, 1active filling agent, high temperature stabilizer, and water, where cementing agent comprises epoxy resin and epoxy resin emulsifier, plasticizer, and nanomaterials.

ZHANG D, ZHANG F, WU X, SONG B, LIU S, LIU J, LI F, LI D

High strength alumina ceramic base material for, e.g. metallurgical applications, comprises alumina, bentonite, composite stabilizer, antifoaming agent, sintering aid, barium sulfate, calcium magnesium mineral and graphene.

OU S, WU X, CHEN Y, ZHANG R

Preparation of graphite thermal field material surface-coated with tantalum carbide coating for high temperature third-generation semiconductor crystal growth furnace, involves high-pressure water treating graphite surface, plasma spraying tantalum powder, infiltrating graphite, and carbonizing.

TANG B, WU X

Method for preparing graphite high heat conducting film used in microelectronic product packaging and integrated field, involves coating CNT and graphene dispersion on graphite film skeleton to perform downward air extraction to obtain graphite with high thermal conductivity membrane.

DENG C, LIU C, LI J, LI H, HONG W, FAN Y, DENG D, TIAN J, CHEN X, WU X

Preparation of graphene heat conducting film, involves mixing graphene oxide slurry and nano-cellulose solution, dispersing, vacuum defoaming, coating graphene oxide/nano-cellulose mixed slurry on two surfaces of fiber fabric, drying, rewinding, carbonizing, graphitizing and roll pressing.

ZHU G, WU X, ZHU Y, TANG W, CHEN Q

Improving dispersibility of graphene reinforced body in non-metallic material matrix comprises adding graphene reinforcing body, non-metallic materials, grinding balls, and grinding auxiliary agent to ball milling tank for ball milling.

JIA B, SHI J, JIANG H, WANG R, ZHU J, WANG Z, LIU B, WU X, CHEN X, ZHANG D, ZHANG W, TANG C

Carbon-based mica board electric heating element used in e.g. electric heating applications, has mica board and conductive coating containing carbon fiber, carbon black, aluminum nitride, glass powder, resistance stabilizer and solvent.

WU H, GENG X, HOU L, XIA L, WU X, HUANG Y, CUI W