Preparing cast aluminum alloy water-soluble precision ceramic core, comprises sieving corundum powder, obtaining phenolic reaction system, forming viscous colloid, mixing and homogenizing corundum glue, graphene oxide mixture, phenolic resin, carbon powder and curing agent and warming.

LIANG C, HU J, ZHANG J, WU G, ZHAO L, LI Y

Use of graphene oxide in improving the density of 3D printing ceramic paste.

XING H, ZHAO H, LAI Q

Rapid prototyping 3D printing material comprises nano alumina, ethylene propylene diene monomer rubber, fumed silica, polyethylene, graphene, polyethylene glycol, rare earth oxide, and reinforcing additives.

CHEN R

Graphene modified silicon carbide ceramic material for bullet-proof armor, comprises graphene, alpha-phase silicon carbide and beta-phase silicon carbide.

WU Y, ZHANG Y, LIU D, LI J, WANG X

High-strength refractory brick includes large andalusite particles, small andalusite particles, large fused silica, medium fused silica, small fused silica, graphene sheet modified nano alumina, nano vanadium oxide and binder.

HE Y

Preparation of graphene oxide nano-material by preparing graphene oxide aqueous solution, adding butanol, standing, water bath heating, standing, suctioning lower layer liquid, and adding remaining liquid with, e.g. tetrabutyl titanate.

LI P, CHEN H, LV J

Preparation of inorganic ceramic coating involves ultrasonically dispersing graphene, mixing with ceramic aggregate and curing agent, mixing resultant mixture with inorganic binder, coating obtained product on base component, and curing.

KWAK Y, BIAN D, ZHAO Y

Graphite-based carbon material used as graphene precursor for preparing graphene dispersion, comprises rhombohedral graphite layer and hexagonal graphite layer, and has specified rate calculated based on X-ray diffraction method.

HASEGAWA S, KAMIYA N, HASEGAWA SHOJI, KAMIYA NAGISA, SHOJI H, NAGISA K, SHEN Y

Graphite-type carbon raw material used as graphene precursor, has rhombohedral system graphite layer and hexagonal system graphite layer in ratio more than preset value, as measured using peak intensities specific planes of layers.

HASEGAWA S, KAMIYA N, SHOJI H, NAGISA K, HASEGAWA SHOJI, KAMIYA NAGISA, SHEN Y