Preparing graphene/polyaniline composite material involves preparing graphene oxide dispersion by subjecting raw materials to Hummers process and high-speed centrifugation to obtain centrifugal liquid, and diluting centrifugal liquid.

CAI Z, LIU Y, MIN Y, FENG Y, CAI J

Graphene dispersant used in e.g. preparation of graphene composite powder, and graphene composite film, comprises polyaniline oligomer or derivative which is electroactive polymer, and combines with graphene via pi-pi bond.

DAI L, GU L, YU H, ZHENG Y, MA J, ZHAO H, LIU S, DING J

Manufacture of polyaniline-reduced graphene oxide composite used as e.g. ink for electromagnetic application, involves mixing graphene oxide dispersion containing emulsifying agent and oligomer solution and oxidizing.

BOCCHINI S, CHIOLERIO A, PORRO S

Composite wear-resistant coating comprises metal substrate comprising iron-based material and composite wear-resistant coating comprising polyimide and solid lubricant comprising fluorinated graphene sheet.

FANG Z, LIU C, WANG J, YANG S, YE X, ZHANG M

Manufacture of aqueous graphene-modified polyurethane film former used as e.g. glass fiber film forming agent, involves adding acetic acid or inorganic acids to terminated polyurethane polymer, reacting and distilling solvent.

HOU Y, LIU H, PAN C, ZHAO J, SUN L, SUN X

Aniline copolymer graphene composite material used for epoxy modified acrylic resin paint has microstructure morphology of sheet shaped reduction oxidation graphene loaded on aniline copolymer nanofiber including 5-amino salicylic acid.

JIANG Y, ZHANG C, ZHU A, WANG H

Aqueous graphene conductive alkyd resin used for conductive coating, comprises ricinoleic acid, neopentyl glycol, trimethylolpropane, m-phenylene, trimellitic anhydride, diethylene glycol butyl ether, butanol, and graphene-xylene solution.

GUO X, ZHANG D

Aqueous antistatic coating used e.g. for plastic substrate, comprises aqueous polyurethane resin, sulfonated graphene/poly(3,4-ethylenedioxythiophene) composite dispersion, crosslinking agent, coupling agent and diluent.

CHEN M, CHEN S, LUAN W

Preparation of polyurethane modified graphene conductive coating used for coating leather, textile, wood or metal surface, includes mixing graphene oxide in deionized water, performing ultrasonic treatment and adding reducing agent.

DUAN B, DIAO S, DING H, WANG X, ZHANG M, WANG Q, WANG S, LUAN Z

Organic-inorganic composite thermally conductive filler used for e.g. thermally conductive thermoplastic resin comprises graphene oxide, hyperbranched polymer, coupling agent, and phenolic resin-coated thermally conductive inorganic filler.

CAO H, YUE L, YAN Y