Heat-resistant graphene film comprises sodium persulfate, graphene oxide, polyethylene wax, ricinoleic acid calcium, aluminium dihydrogen phosphate, diphenyl silanediol, calcium stearate, polyphenyl ether, sorbitan mono-fatty acid ester.

ZHANG Q

Composite material contains epoxy resin, butadiene rubber, terminal carboxylated nitrile rubber, stearic acid, sulfur, N-cyclohexyl-2-benzothiazolesulfenamide, nano titanium dioxide, graphene oxide, and hexaphenoxycyclotriphosphazene.

LI X

Boron nitride-coated sulfonated graphene-epoxy resin composite material for electronic packaging materials, comprises epoxy resin powder, boron nitride powder, sulfonated graphene powder, silane coupling agents, and polyamide curing agent.

CHEN Q, DING X, NI R, DUAN M, LI H

Preparing differential purified terephthalic acid involves mixing bismuth molybdate, graphene oxide, hypochlorous acid solution, zinc oxide, white carbon black, potassium titanate whisker with hydrofluoric acid aqueous solution.

FAN Y, TAO R, HAN W, HU C, YANG X

High-strength composite material for luggage, comprises panel main body and main cloth disposed on surface of panel main body, where panel main body comprises foamed aluminum/graphene composite, polyurethane and functional auxiliary agent.

LI W

Graphene photocurable conductive resin contains epoxy resin, methacrylic acid, aminopolyethylene glycol, graphene, doped polyaniline, isocyanate, sodium aminoethanesulfonate, adipic acid, reactive diluent, catalyst and solvent.

LIN R, ZHUANG Y

Polyurethane heat-insulating plate comprises polyether and modified isocyanate, where combination polyether comprises complex polyol, amines catalyst, foam stabilizer, foaming agent, flame retardant, and modified graphene.

CHEN W

Preparing a special unsaturated resin for automobile putty ash, involves mixing and dispersing graphene oxide, surfactant and water ultrasonically, and then ball-milling, filtering, washing and drying it to obtain pre-oxidized graphene.

WU D, XU Y, HUANG H

Flame-retardant high-temperature nylon graphene composite material comprises e.g. nylon salt, graphene oxide, expanded graphite, silane coupling agent KH560, nano-carbon sol, mica, blocking agent, 6-aminocaproic acid and deionized water.

ZHENG J, ZHANG Q, LI W

High temperature resistant wear-resistant nylon-graphene composite functional material comprises e.g. nylon salt, graphene oxide, brucite fiber, expanded graphite, silane coupling agent KH560, nano carbon sol and nano titanium dioxide.

SU Z, CHEN X