Preparation of modified carbon fiber used as reinforcing material, involves dipping desized carbon fiber in pyrenebutyric acid polyethylene glycol aqueous solution, soaking in graphene oxide water suspension, and drying.

SUN S, LI H, LIU Y, GUO Z, AO Y, MA J, JIN L

Preparing light-weight composite material with excellent mechanical properties at high temperature useful in automobile, by e.g. processing chopped carbon fiber at a high temperature in an ammonia atmosphere, mixing aminated carbon fiber and oxidized carbon modifier, kneading, filtering and molding.

ZHAO L, WANG C, HAN F

Graphene/carbon fiber reinforced nylon 66 composition useful in e.g. automobile industry, comprises nylon 66 resin, expandable graphite, amphiphilic pyrene grafts, ferrimagnetic magnetite modified by oleylamine, polytetrafluoroethylene resin, carbon fiber, and auxiliary agent.

CHEN Y

Composite gel of modified carbon fiber based on asymmetric oxidation graphene useful in mechanical equipment, preferably sensors, capacitors and electrodes comprises water-soluble polymer hydrogel loaded with attached with asymmetric graphene oxide of carbon fiber.

ZHOU S, ZONG L, ZHANG N, ZHANG J, DUAN Y

Preparing nano-reinforced carbon fiber composite material useful in e.g. aerospace, comprises e.g. mixing nano-materials with dispersion working substance, dispersing into gas phase nano-dispersion mist by pulse electric arc, baking, heating, adding epoxy resin, rolling, heating and curing.

GAO C, ZHANG D, WANG Y, SHI S, BI L, ZHANG C, HE Y

Carbon fiber reinforced graphene board, comprises curing sheet, heating film, solidifying sheet, shielding film and solidifying sheet, where curing sheet is prepared by mixing nano-cellulose, graphene and deionized water, performing ultrasonic treatment to obtain mixed solution.

JIN Y

Modifier used in e.g. modified carbon fiber for reinforced resin-based composite material, comprises graphene oxide-aqueous resin composite material comprising graphene oxide and aqueous resin.

LING Y, LIANG M, QIU B, ZOU H

Manufacture of reduced graphene oxide coated carbon fiber reinforced nylon composite material for three-dimensional printing, involves adding composite material of pretreated carbon fiber and shellac solution and nylon particles in ethanol, adding calcium stearate and antioxidant and heating.

LU Z, ZHENG Y

Preparing nylon 12 composite involves alkalizing and modifying coconut shell fiber, using predefined ratio of deionized water, N- (3-dimethylaminopropyl) -N '-ethylcarbodiimide hydrochloride and N-hydroxysuccinimide, forming coconut shell fiber surface grafted graphene oxide, with pyridine compound.

LU Z, ZHENG Y

Modified carbon fiber reinforced polymer-based material useful in preparing spacecraft, space shuttle and space station shellprepared by mixing polymer matrix and curing agent uniformly, using upper slurry to slurry modified carbon fiber and curing.

ZHANG X, LIANG M, ZHANG C, ZOU H