Preparing corrosion resistant coating electrode used for circulating external drainage and desalting comprises polishing and deionized water titanium base plate into acid solution, etching, using cathode and anode salt solution as electrolyte, coating graphene dispersion liquid, and drying.

ZHANG J, MIAO Y, YAN Z, MENG Z, FAN L, LI Y, SONG C, XIU C, ZHANG Q, WU X, XIE X, WANG X

Processing titanium-based nano composite anode for zinc electrodeposition, comprises soaking acidic-etching titanium plate in modified multi-walled carbon nanotubes suspension, reacting, preparing -lead dioxide layer titanium base electrode, cleaning and drying.

LI H, ZHAO C, FENG Z, ZHANG Q, FENG F

Manufacturing titanium fiber used in e.g. biomedical field, comprises subjecting titanium wire to acid washing, pre-nickel plating, and surface copper plating to obtain copper-plated titanium wire, compounding dried copper-plated titanium wire bundled iron pipe, and spraying modified alumina agent.

OUYANG Q, SHUAI G, WEI S, WU X

Modifying surface of titanium substrate useful for fuel cell, involves performing ultrasonic treatment to titanium substrate, placing into vacuum box, performing anode activation, cleaning with organic solvent, and depositing graphene oxide.

ZHAN Y, YAN H, HAO C, HUANG T, YANG M

Preparing antibacterial and corrosion resistant metal orthodontic appliance, involves polishing metal appliance, mixing graphene oxide and nano-silver particles, and adding pretreated metal appliance into electrodeposition solution.

ZHANG C, HE L, DAI D, CHEN Y, WANG J

Preparation of graphene-modified copper-zinc composite coating on titanium alloy involves performing plating treatment using pre-plated titanium alloy as cathode, copper-zinc plate as anode and solution containing copper sulfate.

LI X, XIE X