Preparation of graphene graphite core-sheath structure fiber for e.g. electrochemical electrode and catalyst carrier involves adding carbon fiber in mixture of strong acid and strong oxidizing agent, washing, drying, and thermal peeling.

JI Q, LIU H, ZHAO X, QU J, HU C

Preparation of graphene fiber for e.g. energy storage device involves dispersing graphite oxide in ultrapure water at room temperature, and performing ultrasonic stirring to obtain dilute dispersion of graphite oxide.

HOU C, LI Y, WANG H, SHAO Y, ZHANG Q, HUANG G

Producing nano-mesh fiber membrane for nitro explosive vapor detection, comprises preparing graphene oxide dispersion liquid, preparing graphene oxide black powder, adding triethoxysilane and tetrahydrofuran, and electrostatic spinning.

DOU X, GUO Y, YANG Z, ZU B, GUO L

Preparation of graphene/heat liquid crystal aromatic polyester composite material involves dissolving post-oxidation treatment of graphite oxide in alkenyl ethanol, providing ethanol solution, dispersing and heating.

WANG H, WANG J, WU J, WANG Z, WANG L, ZHOU H

N-doped flexible graphite fiber for e.g. catalyst carrier, is obtained by preparing graphene oxide solution as spinning raw solution, wet-spinning and forming graphene oxide fiber, low-temperature heating, and evaporating solvent.

CHANG Y, HAN G

Preparing graphene modified nylon 6 fiber, useful for e.g. aerospace, comprises adding inorganic acid with graphite powder to obtain purified graphite powder, adding with strong oxidizing acid, filtering, drying to obtain graphene oxide.

DAI L, LU L, HOU W, TANG B

Graphene-oxide-modified phenolic-resin-based ultrafine porous carbon fiber, is prepared in form of micro-porous structure.

HUANG Z, KANG F, BAI Y

Preparation of graphene/silk composite fiber, involves preparing graphene solution using graphite powder and concentrated sulfuric acid, mixing with degummed silk fibroin and formic acid, and electrospinning obtained solution.

SONG C, XIAO J, FENG Y, LUO Y, WU S