Preparing bacterial cellulose composite fiber comprises soaking grown bacterial cellulose membrane with alkaline solution, cutting and crushing, adding freeze-dried bacterial cellulose into calcium chloride/acid dissolving system, extruding, and heat-stretching primary composite fiber in water bath.

ZHANG G, DANG X, HU X, BAI Y

Preparing silver/graphene composite fiber involves preparing large sheets of graphene oxide by the improved Hummers method, preparing graphene oxide water dispersion as spinning solution, and filling the solution into a needle cylinder.

QU J, SHEN M, QIAN J, LI Y, WANG R, HU X

Preparation of graphene-polyvinyl alcohol functional composite fibers used in e.g. building application, involves forming jelly filaments using solution of graphene, polyvinyl alcohol and gelling agent, and thermally stretching.

BAI Y, HU X, SHA Y, SHA X

Preparation of high-strength polyacrylonitrile nanocomposite fiber involves taking organic solvent or mixed solution of organic solvent and water, adding graphene, doping, filtering, degassing, coagulating, extracting, and heat stretching.

BAI Y, HU X, SHA X, SHA Y

Preparation of high-strength and high-modulus polyvinyl alcohol-graphene nanocomposite fibers used for e.g. building material, involves mixing graphene and polyvinyl alcohol in mixed solvent, spinning and hot-stretching mixture.

BAI Y, HU X, SHA X, SHA Y

Graphene composite fiber comprises graphene sheet, and polymer comprising hyperbranched polymers and/or polyvinyl alcohol and aggregating graphene sheet formed regularly along axial direction of composite fiber.

GAO C, HU X, XU Y, ZHOU X