Preparing sulfonated modified graphene oxide-based superhydrophobic magnesium alloy surface comprises e.g. pre-treating magnesium alloy, ultrasonically cleaning with isopropanol and acetone, removing organic matter and drying.

CHEN Y

Preparing sulfonated modified graphene oxide-based superhydrophobic copper-nickel alloy surface comprises e.g. first polishing copper nickel alloy through sand paper to removing impurities and oxides on surface and ultrasonically cleaning.

CHEN Y

Preparing graphene-based superhydrophobic B30 copper-nickel alloy involves polishing B30 copper-nickel alloy with sandpaper to remove impurities and oxides on the surface, using absolute ethanol and ultrasonic cleaning.

LIU Y, CHEN Y

Preparing graphene-based superhydrophobic low-carbon steel involves polishing low-carbon steel first with sandpaper respectively to remove impurities and oxides on surface, and ultrasonically cleaning with absolute ethanol and acetone.

YANG Z, CHEN Y

Preparing graphene-based superhydrophobic magnesium alloy comprises polishing magnesium alloy, ultrasonically cleaning using isopropanol and acetone, drying using nitrogen and performing electro-deposition using electrolyte composition.

CHEN Y

Preparation of graphene-based super-hydrophobic stainless steel involves polishing and cleaning stainless steel, drying, and performing electrodeposition using electrolyte formulation containing graphene oxide and linolenic acid.

CHEN Y

Preparation of superhydrophobic copper-nickel alloy involves pretreating copper-nickel alloy, and forming superhydrophobic structure by electrodeposition using electrolyte containing graphene oxide, linolenic acid and benzotriazole.

CHEN Y

Preparation of graphene-based superhydrophobic aluminum alloy, involves cleaning aluminum alloy, and preparing structure by electrodeposition using electrolyte comprising graphene oxide, linolenic acid, and absolute ethanol.

CHEN Y

High-temperature resistant and anticorrosive conductive paint comprises organic silicon modified epoxy resin, polyamide curing agent, solvent, graphene, babbitt alloy powder, mica powder, mica iron oxide powder, talcum powder.

LIU Z

Conductive coating used for high current lightning strikes, comprises epoxy resin, polyamide curing agent, solvent, zinc powder, graphene, tin powder, mica powder, talc powder, toughening agent, gas phase silica, organic bentonite.