Manufacture of silicone rubber interface material for electronic product, involves adding surfactant to toluene, adding graphene, ultrasonic processing, adding filler and silicone rubber, adding silicone oil and catalyst, and molding.

FENG Y, LIU L, LU Y, WANG X, ZHANG J, ZHANG L

Making magnetic nano-graphene oxide involves preparing oxidized graphite alkene using Hummers method; and loading ferroferric oxide nano-particle on surface of magnetic nano graphene oxide in alkaline condition using hydro-thermal method.

ZHANG F, LI B, LI Q, JI G, FENG Y, AO R, LV M

Large-size stacked structure of graphene wafer used in e.g. silicon-based semiconductor device, is provided with single crystal graphene layer, boron nitride layer, single crystal boron nitride layer and silicon dioxide wafer substrate.

GUO C, MA Z, ZHANG P, WU Y, ZHUANG Y, XIAO Z, FENG Y, ZHAO Y

Multi-layer graphene double-grid FET for use in high frequency large power device, has transistor unit formed with multiple layers, where source and drain electrodes of transistor unit are connected together in parallel manner.

GUO C, MA Z, ZHANG P, WU Y, ZHUANG Y, XIAO Z, FENG Y, ZHAO Y

Preparation of graphene/silk composite fiber, involves preparing graphene solution using graphite powder and concentrated sulfuric acid, mixing with degummed silk fibroin and formic acid, and electrospinning obtained solution.

SONG C, XIAO J, FENG Y, LUO Y, WU S

Preparation of graphene comprises mixing aqueous solution of graphene oxide solution and food antioxidant solution containing citric acid, performing reduction reaction, washing, removing unreacted oxide and food antioxidant, and drying.

FENG Y, LUO Y

Forming graphene nano alloy composite material as a carrier involves mixing noble/transition metal salt solution with graphene oxide aqueous solution, adjusting pH, adding reducing agent, then placing in furnace under inert gas protection.

LIN X, XU C, YAO Y, FENG Y

Microwave-assisted sodium citrate reduction method for preparing graphene comprises using Hummers method to prepare graphite oxide, dispersing in deionized water, ultrasonically dispersing and reacting with sodium citrate.

YAN H, MAO K, LI S, FENG Y, LIU C

Functionalized graphene used for forming polyethylene composite material, is obtained by condensing graphite oxide and triethoxy octyl silane, ultrasonically dispersing modified graphite in oleic acid, and reacting.

WANG G, FENG Y, LU Z, YU J, JIANG Y

Preparing silica gel material covered graphene comprises preparing graphene oxide and silica gel dispersion liquids and then mixing, adding mixing solution with amino silica gel and oxidized graphite alkene and then stirring.

ZHU G, FENG Y, LUO Y